Fire Resistance, Thermal and Anti-Ageing Properties of Transparent Fire-Retardant Coatings Modified with Different Molecular Weights of Polyethylene Glycol Borate
Four kinds of polyethylene glycol borate (PEG-BA) with different molecular weights were grafted into cyclic phosphate ester (PEA) to obtain flexible phosphate esters (PPBs), and then applied in amino resin to obtain a series of transparent intumescent fire-retardant coatings. The comprehensive prope...
Main Authors: | Long Yan, Xinyu Tang, Xiaojiang Xie, Zhisheng Xu |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2021-11-01
|
Series: | Polymers |
Subjects: | |
Online Access: | https://www.mdpi.com/2073-4360/13/23/4206 |
Similar Items
-
Facile Fabrication of Multifunctional Transparent Flame-Retarded Hydrogel for Fire-Resistant Glass with Excellent Transparency, Fire Resistance and Anti-Ageing Property
by: Feiyue Wang, et al.
Published: (2022-07-01) -
A Nitrogen-Rich DOPO-Based Derivate for Increasing Fire Resistance of Epoxy Resin with Comparable Transparency
by: Jiayi Lu, et al.
Published: (2023-01-01) -
Comparative Study of Fire Resistance and Char Formation of Intumescent Fire-Retardant Coatings Reinforced with Three Types of Shell Bio-Fillers
by: Feiyue Wang, et al.
Published: (2021-12-01) -
Effect of the B:Zn:H<sub>2</sub>O Molar Ratio on the Properties of Poly(Vinyl Acetate) and Zinc Borate-Based Intumescent Coating Materials Exposed to a Quasi-Real Cellulosic Fire
by: Jakub Łopiński, et al.
Published: (2020-10-01) -
Comparative Study of Fire Resistance and Anti-Ageing Properties of Intumescent Fire-Retardant Coatings Reinforced with Conch Shell Bio-Filler
by: Feiyue Wang, et al.
Published: (2021-08-01)