| Summary: | The synthesis of gasoline-range hydrocarbons by gas-phase dimethyl ether (DME) conversion was investigated on various ZSM-5 zeolites with different morphologies and Fe contents. The different morphologies of ZSM-5 significantly altered the distributions of the acidic sites, which showed different selectivities to gasoline-range hydrocarbons. Nanostructured ZSM-5 (N-ZSM-5) revealed the highest C<sub>5+</sub> selectivity of 41.7% with an aromatics selectivity of 23.6% at ~100% DME conversion. The superior catalytic activity of N-ZSM-5 was attributed to the largest strong Brønsted acidic sites and smaller crystallite sizes, which were beneficial for the faster removal rate of heavy hydrocarbons due to its shorter diffusion pathlength compared to conventional ZSM-5 (C-ZSM-5). In addition, 10 wt% Fe-impregnated N-ZSM-5 revealed an enhanced C<sub>5+</sub> selectivity of 60.6% with a smaller C<sub>1</sub>–C<sub>4</sub> selectivity of 21.9%, which were attributed to the adjusted acidic sites by suppressing the cracking reactions of the surface intermediates, which are responsible for the selective formation of smaller light hydrocarbons. However, the excess amount of Fe on N-ZSM-5 showed a lower DME conversion of 83.5% with a lower C<sub>5+</sub> selectivity of 38.5% due to the blockages of the active acidic sites. Nanostructured N-ZSM-5 possessing a larger amount of strong Brønsted acid sites with 10 wt% Fe modification clearly showed a higher formation rate of gasoline-range hydrocarbons due to an enhanced secondary oligomerization of surface intermediates to form heavier aromatic hydrocarbons.
|
|---|