| Summary: | In this work, polyamide 6 (PA6) properties were tailored and improved using a maleic anhydride-grafted acrylonitrile-butadiene-styrene terpolymer (ABS-MA). The PA6/ABS-MA blends were prepared using a co-rotational twin-screw extruder. Subsequently, the extruded pellets were injection-molded. Blends were characterized by torque rheometry, the Molau test, Fourier transform infrared spectroscopy (FTIR), impact strength, tensile strength, Heat Deflection Temperature (HDT), Differential Scanning Calorimetry (DSC), Thermogravimetry (TG), Contact Angle, Scanning Electron Microscopy (SEM), and water absorption experiments. The most significant balance of properties, within the analyzed content range (5, 7.5, and 10 wt.%), was obtained for the PA6/ABS-MA (10%) blend, indicating that even low concentrations of ABS-MA can improve the properties of PA6. Significant increases in impact strength and elongation at break have been achieved compared with PA6. The elastic modulus, tensile strength, HDT, and thermal stability properties of the PA6/ABS-MA blends remained at high levels, indicating that maleic anhydride interacted with amine end-groups of PA6. Torque rheometry, the Molau test, and SEM analysis suggested interactions in the PA6/ABS-MA system, confirming the high properties obtained. Additionally, there was a decrease in water absorption and the diffusion coefficient of the PA6/ABS-MA blends, corroborating the contact angle analysis.
|
|---|