| Summary: | Austenitic-ferritic stainless steels are alloys with controlled additions of Cr, Ni, Mo and N which, after a suitable thermomechanical treatment, results in a balanced microstructure with similar proportions of ferrite (δ) and austenite (γ). Thus, it is possible to obtain good combinations of high mechanical properties and corrosion resistance through microstructural refinement, which also leads to a relatively good Pitting Resistance Equivalent value (PRE) at both phases. However, inadequate heat treatment and/or welding processes might result in the precipitation of deleterious phases, leading to poor mechanical properties and/or corrosion resistance. In this sense, the use of non-destructive microstructural characterization techniques becomes a valuable resource to access such alterations. Therefore, this work evaluates the precipitation of deleterious phase’s in welded thermal aged joints by portable Double Loop Electrochemical Polarization Reactivation (DL-EPR) taking into account a preliminary metallographic replica characterization. The results show that the proposed portable method can detect even a small percentage of deleterious phases, in addition to having a strong potential to be a non-destructive microstructural characterization technique.
|
|---|