Effect of Revolutionary Pitch on Interface Microstructure and Mechanical Behavior of Friction Stir Lap Welds of AA6082-T6 to Galvanized DP800
Friction stir lap welding of 1.5-mm thick 6082-T6 aluminum alloy to 2-mm thick galvanized DP800 steel (Zn-coated) was carried out. Optimal welding conditions were obtained aiming to defect-free joints with good mechanical properties. The interfacial intermetallic compounds (IMCs) at the stir zone an...
| Main Authors: | , , , , |
|---|---|
| Formato: | Artigo |
| Idioma: | English |
| Publicado em: |
MDPI AG
2018-11-01
|
| Colecção: | Metals |
| Assuntos: | |
| Acesso em linha: | https://www.mdpi.com/2075-4701/8/11/925 |