Caracterización de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 mediante las técnicas de Reducción Térmica Programada (TPR), Desorción Térmica Programada (TPD) y Análisis Térmico Gravimétrico (TGA) Characterization of Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 by means of Thermal Programmed Reduction (TPR), Thermal Programmed Desorption (TPD) and Thermal Gravimetric Analysis (TGA)
Resumen Se preparó un catalizador de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 y fue caracterizado mediante las técnicas de TPD de H2 y O2, TPR, y TGA. Como muestras de referencia se prepararon catalizadores más simples del tipo Pd/CeO2 y Pd/Al2O3. Se observó una progresiva desactivación en los catalizadores Pd/C...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universidad del Zulia
2002-12-01
|
| Series: | Revista Técnica de la Facultad de Ingeniería |
| Subjects: | |
| Online Access: | http://wwww.scielo.org.ve/scielo.php?script=sci_arttext&pid=S0254-07702002000300003 |
| _version_ | 1818954102698147840 |
|---|---|
| author | Dora M. Finol Adriana I. Moncada Z. Jonathan E. Méndez M. Jorge L. Sánchez A. Hilario Vidal M. |
| author_facet | Dora M. Finol Adriana I. Moncada Z. Jonathan E. Méndez M. Jorge L. Sánchez A. Hilario Vidal M. |
| author_sort | Dora M. Finol |
| collection | DOAJ |
| description | Resumen Se preparó un catalizador de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 y fue caracterizado mediante las técnicas de TPD de H2 y O2, TPR, y TGA. Como muestras de referencia se prepararon catalizadores más simples del tipo Pd/CeO2 y Pd/Al2O3. Se observó una progresiva desactivación en los catalizadores Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 y Pd/Al2O3 conforme aumenta la temperatura de reducción, la cual es significativa a 700°C. El Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 experimenta cambios irreversibles cuando se somete a tratamientos a elevadas temperaturas (900°C). Los estudios de TPR demostraron que la reducción del Pd ocurre en dos etapas, y que el Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 se reduce en un intervalo de temperaturas mucho mayor que el observado en el catalizador Pd/CeO2. En los diagramas de TGA de los catalizadores Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 y Pd/Al2O3 se observó la existencia de fenómenos de histéresis en el par redox PdO « Pdº. Como lo demuestran estos resultados y los de TPD de O2, en el óxido mixto de Ce/Tb soportado se favorece la oxidación del paladio a más altas temperaturas que las observadas en el catalizador Pd/Al2O3.<br>Abstract A Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 catalyst was prepared and characterized by using TPD of H2 and O2, TPR and TGA measurements. Pd/CeO2 and Pd/Al2O3 catalysts were used as reference samples. Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 and Pd/Al2O3 catalysts showed a deactivation with the increase of the reduction temperature, specially at 700°C. The Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 catalyst had irreversible changes when it is heated at high temperatures (900°C). The studies of TPR showed that the Pd is reduced in two steps, and that the Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 catalyst is reduced in a larger interval of temperature than the Pd/CeO2 catalyst. In the TGA diagrams of Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 and Pd/Al2O3 catalysts, was observed the existence of hysteresis in the redox couple PdO « Pdº. These results, in good agreement with the TPD-O2 ones, showed that in the supported mixed oxide of Ce/Tb the palladium oxidation occurs at higher temperatures than in the Pd/Al2O3 catalyst. |
| first_indexed | 2024-12-20T10:16:50Z |
| format | Article |
| id | doaj.art-6c8e6d3ba0d245fd9c8b523bce88a855 |
| institution | Directory Open Access Journal |
| issn | 0254-0770 |
| language | English |
| last_indexed | 2024-12-20T10:16:50Z |
| publishDate | 2002-12-01 |
| publisher | Universidad del Zulia |
| record_format | Article |
| series | Revista Técnica de la Facultad de Ingeniería |
| spelling | doaj.art-6c8e6d3ba0d245fd9c8b523bce88a8552022-12-21T19:44:02ZengUniversidad del ZuliaRevista Técnica de la Facultad de Ingeniería0254-07702002-12-01253149157Caracterización de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 mediante las técnicas de Reducción Térmica Programada (TPR), Desorción Térmica Programada (TPD) y Análisis Térmico Gravimétrico (TGA) Characterization of Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 by means of Thermal Programmed Reduction (TPR), Thermal Programmed Desorption (TPD) and Thermal Gravimetric Analysis (TGA)Dora M. FinolAdriana I. Moncada Z.Jonathan E. Méndez M.Jorge L. Sánchez A.Hilario Vidal M.Resumen Se preparó un catalizador de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 y fue caracterizado mediante las técnicas de TPD de H2 y O2, TPR, y TGA. Como muestras de referencia se prepararon catalizadores más simples del tipo Pd/CeO2 y Pd/Al2O3. Se observó una progresiva desactivación en los catalizadores Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 y Pd/Al2O3 conforme aumenta la temperatura de reducción, la cual es significativa a 700°C. El Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 experimenta cambios irreversibles cuando se somete a tratamientos a elevadas temperaturas (900°C). Los estudios de TPR demostraron que la reducción del Pd ocurre en dos etapas, y que el Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 se reduce en un intervalo de temperaturas mucho mayor que el observado en el catalizador Pd/CeO2. En los diagramas de TGA de los catalizadores Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 y Pd/Al2O3 se observó la existencia de fenómenos de histéresis en el par redox PdO « Pdº. Como lo demuestran estos resultados y los de TPD de O2, en el óxido mixto de Ce/Tb soportado se favorece la oxidación del paladio a más altas temperaturas que las observadas en el catalizador Pd/Al2O3.<br>Abstract A Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 catalyst was prepared and characterized by using TPD of H2 and O2, TPR and TGA measurements. Pd/CeO2 and Pd/Al2O3 catalysts were used as reference samples. Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 and Pd/Al2O3 catalysts showed a deactivation with the increase of the reduction temperature, specially at 700°C. The Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 catalyst had irreversible changes when it is heated at high temperatures (900°C). The studies of TPR showed that the Pd is reduced in two steps, and that the Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 catalyst is reduced in a larger interval of temperature than the Pd/CeO2 catalyst. In the TGA diagrams of Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 and Pd/Al2O3 catalysts, was observed the existence of hysteresis in the redox couple PdO « Pdº. These results, in good agreement with the TPD-O2 ones, showed that in the supported mixed oxide of Ce/Tb the palladium oxidation occurs at higher temperatures than in the Pd/Al2O3 catalyst.http://wwww.scielo.org.ve/scielo.php?script=sci_arttext&pid=S0254-07702002000300003Catalizadores de tres víasTPD de H2TPD de O2TPR y TGA.Three way catalystsTPD - H2, TPD - O2TPR and TGA. |
| spellingShingle | Dora M. Finol Adriana I. Moncada Z. Jonathan E. Méndez M. Jorge L. Sánchez A. Hilario Vidal M. Caracterización de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 mediante las técnicas de Reducción Térmica Programada (TPR), Desorción Térmica Programada (TPD) y Análisis Térmico Gravimétrico (TGA) Characterization of Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 by means of Thermal Programmed Reduction (TPR), Thermal Programmed Desorption (TPD) and Thermal Gravimetric Analysis (TGA) Revista Técnica de la Facultad de Ingeniería Catalizadores de tres vías TPD de H2 TPD de O2 TPR y TGA. Three way catalysts TPD - H2, TPD - O2 TPR and TGA. |
| title | Caracterización de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 mediante las técnicas de Reducción Térmica Programada (TPR), Desorción Térmica Programada (TPD) y Análisis Térmico Gravimétrico (TGA) Characterization of Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 by means of Thermal Programmed Reduction (TPR), Thermal Programmed Desorption (TPD) and Thermal Gravimetric Analysis (TGA) |
| title_full | Caracterización de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 mediante las técnicas de Reducción Térmica Programada (TPR), Desorción Térmica Programada (TPD) y Análisis Térmico Gravimétrico (TGA) Characterization of Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 by means of Thermal Programmed Reduction (TPR), Thermal Programmed Desorption (TPD) and Thermal Gravimetric Analysis (TGA) |
| title_fullStr | Caracterización de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 mediante las técnicas de Reducción Térmica Programada (TPR), Desorción Térmica Programada (TPD) y Análisis Térmico Gravimétrico (TGA) Characterization of Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 by means of Thermal Programmed Reduction (TPR), Thermal Programmed Desorption (TPD) and Thermal Gravimetric Analysis (TGA) |
| title_full_unstemmed | Caracterización de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 mediante las técnicas de Reducción Térmica Programada (TPR), Desorción Térmica Programada (TPD) y Análisis Térmico Gravimétrico (TGA) Characterization of Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 by means of Thermal Programmed Reduction (TPR), Thermal Programmed Desorption (TPD) and Thermal Gravimetric Analysis (TGA) |
| title_short | Caracterización de Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 mediante las técnicas de Reducción Térmica Programada (TPR), Desorción Térmica Programada (TPD) y Análisis Térmico Gravimétrico (TGA) Characterization of Pd/Ce0.8Tb0.2Ox/La2O3-Al2O3 by means of Thermal Programmed Reduction (TPR), Thermal Programmed Desorption (TPD) and Thermal Gravimetric Analysis (TGA) |
| title_sort | caracterizacion de pd ce0 8tb0 2ox la2o3 al2o3 mediante las tecnicas de reduccion termica programada tpr desorcion termica programada tpd y analisis termico gravimetrico tga characterization of pd ce0 8tb0 2ox la2o3 al2o3 by means of thermal programmed reduction tpr thermal programmed desorption tpd and thermal gravimetric analysis tga |
| topic | Catalizadores de tres vías TPD de H2 TPD de O2 TPR y TGA. Three way catalysts TPD - H2, TPD - O2 TPR and TGA. |
| url | http://wwww.scielo.org.ve/scielo.php?script=sci_arttext&pid=S0254-07702002000300003 |
| work_keys_str_mv | AT doramfinol caracterizaciondepdce08tb02oxla2o3al2o3mediantelastecnicasdereducciontermicaprogramadatprdesorciontermicaprogramadatpdyanalisistermicogravimetricotgacharacterizationofpdce08tb02oxla2o3al2o3bymeansofthermalprogrammedreductiontprthermalprogrammeddesorptiont AT adrianaimoncadaz caracterizaciondepdce08tb02oxla2o3al2o3mediantelastecnicasdereducciontermicaprogramadatprdesorciontermicaprogramadatpdyanalisistermicogravimetricotgacharacterizationofpdce08tb02oxla2o3al2o3bymeansofthermalprogrammedreductiontprthermalprogrammeddesorptiont AT jonathanemendezm caracterizaciondepdce08tb02oxla2o3al2o3mediantelastecnicasdereducciontermicaprogramadatprdesorciontermicaprogramadatpdyanalisistermicogravimetricotgacharacterizationofpdce08tb02oxla2o3al2o3bymeansofthermalprogrammedreductiontprthermalprogrammeddesorptiont AT jorgelsancheza caracterizaciondepdce08tb02oxla2o3al2o3mediantelastecnicasdereducciontermicaprogramadatprdesorciontermicaprogramadatpdyanalisistermicogravimetricotgacharacterizationofpdce08tb02oxla2o3al2o3bymeansofthermalprogrammedreductiontprthermalprogrammeddesorptiont AT hilariovidalm caracterizaciondepdce08tb02oxla2o3al2o3mediantelastecnicasdereducciontermicaprogramadatprdesorciontermicaprogramadatpdyanalisistermicogravimetricotgacharacterizationofpdce08tb02oxla2o3al2o3bymeansofthermalprogrammedreductiontprthermalprogrammeddesorptiont |