EFFECT OF TWO YEARS NATURAL AGING ON BURST PRESSURE OF OVER-PRESSURE COPPER TUBE (MT)
To study the stability of the over-pressure reinforcement effect of the copper tube at room temperature, the burst tests for the small diameter soft TP2 copper tube at room temperature during the natural aging time of 0, 6, 12 and 24 months were carried out respectively. These results indicated that...
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Editorial Office of Journal of Mechanical Strength
2023-01-01
|
| Series: | Jixie qiangdu |
| Subjects: | |
| Online Access: | http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2023.02.014 |
| _version_ | 1826870520885280768 |
|---|---|
| author | YANG Fan LUO Feng LIU Bing ZHANG HongWei FAN YouXiong LIU XiaoNing |
| author_facet | YANG Fan LUO Feng LIU Bing ZHANG HongWei FAN YouXiong LIU XiaoNing |
| author_sort | YANG Fan |
| collection | DOAJ |
| description | To study the stability of the over-pressure reinforcement effect of the copper tube at room temperature, the burst tests for the small diameter soft TP2 copper tube at room temperature during the natural aging time of 0, 6, 12 and 24 months were carried out respectively. These results indicated that: the mean of the measured burst pressure did not change significantly for small diameter soft TP2 copper bare tube and rifled tube at the same pretreatment pressure during the natural aging time of 0, 6, 12 and 24 months, respectively. The standard deviation was gradually smaller and the over-pressure strengthening effect was obvious. The measured burst pressure was different obviously for small diameter soft TP2 copper tube at the pretreatment pressure was 4.60 MPa and 16.50 MPa respectively during the same natural aging time, the mean was significantly larger and standard deviation was significantly smaller for measured burst pressure with the increase of pretreatment pressure, the results showed that pretreatment pressure had a great influence on strengthening effect, and higher pretreatment pressure could get better strengthening effect. The burst pressure conforms to the normal distribution for the same small diameter soft TP2 copper tube at the same over-pressure reinforcement during the natural aging time shall not exceed 24 months. Over-pressure reinforcement at room temperature was a suitable method to increase burst pressure of soft TP2 copper tube, and the method could be used in engineering. |
| first_indexed | 2024-03-12T20:41:10Z |
| format | Article |
| id | doaj.art-6ca83dcb4c994b9f90877a05e93bdcf2 |
| institution | Directory Open Access Journal |
| issn | 1001-9669 |
| language | zho |
| last_indexed | 2025-02-16T23:26:47Z |
| publishDate | 2023-01-01 |
| publisher | Editorial Office of Journal of Mechanical Strength |
| record_format | Article |
| series | Jixie qiangdu |
| spelling | doaj.art-6ca83dcb4c994b9f90877a05e93bdcf22025-01-15T02:40:11ZzhoEditorial Office of Journal of Mechanical StrengthJixie qiangdu1001-96692023-01-0135736536351246EFFECT OF TWO YEARS NATURAL AGING ON BURST PRESSURE OF OVER-PRESSURE COPPER TUBE (MT)YANG FanLUO FengLIU BingZHANG HongWeiFAN YouXiongLIU XiaoNingTo study the stability of the over-pressure reinforcement effect of the copper tube at room temperature, the burst tests for the small diameter soft TP2 copper tube at room temperature during the natural aging time of 0, 6, 12 and 24 months were carried out respectively. These results indicated that: the mean of the measured burst pressure did not change significantly for small diameter soft TP2 copper bare tube and rifled tube at the same pretreatment pressure during the natural aging time of 0, 6, 12 and 24 months, respectively. The standard deviation was gradually smaller and the over-pressure strengthening effect was obvious. The measured burst pressure was different obviously for small diameter soft TP2 copper tube at the pretreatment pressure was 4.60 MPa and 16.50 MPa respectively during the same natural aging time, the mean was significantly larger and standard deviation was significantly smaller for measured burst pressure with the increase of pretreatment pressure, the results showed that pretreatment pressure had a great influence on strengthening effect, and higher pretreatment pressure could get better strengthening effect. The burst pressure conforms to the normal distribution for the same small diameter soft TP2 copper tube at the same over-pressure reinforcement during the natural aging time shall not exceed 24 months. Over-pressure reinforcement at room temperature was a suitable method to increase burst pressure of soft TP2 copper tube, and the method could be used in engineering.http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2023.02.014Natural agingSmall diameterTP2 copper pipeOver-pressure reinforcementBurst pressureStability |
| spellingShingle | YANG Fan LUO Feng LIU Bing ZHANG HongWei FAN YouXiong LIU XiaoNing EFFECT OF TWO YEARS NATURAL AGING ON BURST PRESSURE OF OVER-PRESSURE COPPER TUBE (MT) Jixie qiangdu Natural aging Small diameter TP2 copper pipe Over-pressure reinforcement Burst pressure Stability |
| title | EFFECT OF TWO YEARS NATURAL AGING ON BURST PRESSURE OF OVER-PRESSURE COPPER TUBE (MT) |
| title_full | EFFECT OF TWO YEARS NATURAL AGING ON BURST PRESSURE OF OVER-PRESSURE COPPER TUBE (MT) |
| title_fullStr | EFFECT OF TWO YEARS NATURAL AGING ON BURST PRESSURE OF OVER-PRESSURE COPPER TUBE (MT) |
| title_full_unstemmed | EFFECT OF TWO YEARS NATURAL AGING ON BURST PRESSURE OF OVER-PRESSURE COPPER TUBE (MT) |
| title_short | EFFECT OF TWO YEARS NATURAL AGING ON BURST PRESSURE OF OVER-PRESSURE COPPER TUBE (MT) |
| title_sort | effect of two years natural aging on burst pressure of over pressure copper tube mt |
| topic | Natural aging Small diameter TP2 copper pipe Over-pressure reinforcement Burst pressure Stability |
| url | http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2023.02.014 |
| work_keys_str_mv | AT yangfan effectoftwoyearsnaturalagingonburstpressureofoverpressurecoppertubemt AT luofeng effectoftwoyearsnaturalagingonburstpressureofoverpressurecoppertubemt AT liubing effectoftwoyearsnaturalagingonburstpressureofoverpressurecoppertubemt AT zhanghongwei effectoftwoyearsnaturalagingonburstpressureofoverpressurecoppertubemt AT fanyouxiong effectoftwoyearsnaturalagingonburstpressureofoverpressurecoppertubemt AT liuxiaoning effectoftwoyearsnaturalagingonburstpressureofoverpressurecoppertubemt |