Experimental Investigation of the Phase Relations in the Fe-Zr-Y Ternary System
The phase relations of the Fe-Zr-Y system at 973 K and 1073 K were experimentally investigated by using the equilibrated alloys. New ternary compounds τ3-Fe<sub>3</sub>ZrY and τ4-Fe<sub>10</sub>Zr<sub>5</sub>Y<sub>2</sub> were found in this ternary sys...
Main Authors: | , , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2022-01-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/15/2/593 |
Summary: | The phase relations of the Fe-Zr-Y system at 973 K and 1073 K were experimentally investigated by using the equilibrated alloys. New ternary compounds τ3-Fe<sub>3</sub>ZrY and τ4-Fe<sub>10</sub>Zr<sub>5</sub>Y<sub>2</sub> were found in this ternary system. The solubility of Y in Fe<sub>2</sub>Zr was measured to be 3.5 at.% and the third component can hardly dissolve in the other binary intermetallic phases. Experiments have verified that Fe<sub>2.9</sub>Zr<sub>0.5</sub>Y<sub>0.5</sub> has a solid solubility ranging from Fe73Zr12Y14 to Fe77Zr9Y13. |
---|---|
ISSN: | 1996-1944 |