Effect of zirconium oxide nanofiber on the strength and chloride ion penetration coefficient of concrete
Abstract In this study, zirconium oxide nanofiber with a mean diameter of 100 nm was added to concrete at various concentrations as a cement replacement. Various tests, including compressive strength, splitting tensile strength, flexural strength, and electrical resistance tests, as well as a rapid...
Main Authors: | Yaser Zarea, Saeed Parhoodeh, Leila Shahryari, Ali Karbakhsh |
---|---|
Format: | Article |
Language: | English |
Published: |
Springer
2023-08-01
|
Series: | SN Applied Sciences |
Subjects: | |
Online Access: | https://doi.org/10.1007/s42452-023-05471-z |
Similar Items
-
Synthesizing and Characterization of Monoclinic and Tetragonal Phases of Zirconium Oxide (Zro2) Nanofibers with the Aid of Electrospinning Technique
by: Yaser Zarea, et al.
Published: (2020-05-01) -
Chloride Ion-Selective Electrode with Solid-Contact Based on Polyaniline Nanofibers and Multiwalled Carbon Nanotubes Nanocomposite
by: Karolina Pietrzak, et al.
Published: (2022-11-01) -
Mechanical Strength and Chloride Ions’ Penetration of Alkali-Activated Concretes (AAC) with Blended Precursor
by: Patrycja Duży, et al.
Published: (2022-06-01) -
Time-Dependency in the Corrosion Process of Reinforced Concrete Subjected to a Chloride Solution
by: Sangki Park, et al.
Published: (2023-11-01) -
Effect of Chloride Ions on the Electrochemical Oxidation of Chalcopyrite at 340 °C and 21 MPa
by: Luying Wang, et al.
Published: (2020-11-01)