Effect of tooth age on bond strength to dentin Efeito da idade na resistência de união
This in vitro study evaluated the effect of tooth age on the tensile bond strength of Prime & Bond NT adhesive system to dentin. Human third molars from the five age groups were analyzed: A- 17 to 20yrs, B- 21 to 30yrs, C- 31 to 40yrs, D- 41 to 50yrs and E- 51 to 63yrs. The occlusal enamel was r...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of São Paulo
2003-12-01
|
| Series: | Journal of Applied Oral Science |
| Subjects: | |
| Online Access: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572003000400013 |
| _version_ | 1819231076770381824 |
|---|---|
| author | Marcelo Giannini Patrícia Chaves Marcelo Tavares de Oliveira |
| author_facet | Marcelo Giannini Patrícia Chaves Marcelo Tavares de Oliveira |
| author_sort | Marcelo Giannini |
| collection | DOAJ |
| description | This in vitro study evaluated the effect of tooth age on the tensile bond strength of Prime & Bond NT adhesive system to dentin. Human third molars from the five age groups were analyzed: A- 17 to 20yrs, B- 21 to 30yrs, C- 31 to 40yrs, D- 41 to 50yrs and E- 51 to 63yrs. The occlusal enamel was removed using a diamond saw under water cooling and the dentin surface was wet-ground with 600-grit SiC paper to obtain flat surfaces. The adhesive system was applied according to the manufacturer's instructions and a 6-mm high resin "crown" was built-up with resin composite. Teeth were stored for 24 hours in distilled water at 37ºC and prepared for micro-tensile testing. Each specimen was mounted in a testing jig attached to a universal testing machine and stressed in tension at a crosshead speed of 0.5mm/min until failure. The means of tensile bond strength were (MPa): A- 21.42 ± 7.52ª; B- 30.13 ± 10.19ª; C- 31.69 ± 11.78ª; D- 30.69 ± 8.47ª and E- 35.66 ± 9.54ª. No statistically significant difference was observed among the age groups (p > 0.05). The results suggested that the tensile bond strength of the adhesive system was not significantly affected by dentin aging.<br>Este estudo avaliou, in vitro, o efeito da idade na resistência à tração do sistema adesivo Prime & Bond NT no substrato dentinário. Foram utilizados terceiros molares humanos de cinco faixas etárias: A- 17 a 20, B- 21 a 30, C- 31 a 40, D- 41 a 50 e E- 51 a 63. O esmalte oclusal foi removido utilizando disco de diamante e a superfície dentinária abrasionada e planificada com lixa de SiC (600) sob refrigeração. O sistema adesivo foi aplicado de acordo com as recomendações do fabricante e um bloco de resina composta de 6 mm de altura foi confeccionado na superfície dentinária. Os dentes foram armazenados em água por 24 horas a 37ºC e preparados para o ensaio de micro-tração. Cada espécime foi fixado no dispositivo de micro-tração que estava acoplado a uma máquina universal de ensaio e testado numa velocidade de 0,5 mm/min. As médias de resistência à tração foram (MPa): A- 21,42 ± 7,52ª; B- 30,13 ± 10,19ª; C- 31,69 ± 11,78ª; D- 30,69 ± 8,47ª e E- 35,66 ± 9,54ª. Nenhuma diferença significativa foi observada entre os grupos formados pelas faixas etárias (p > 0,05). Os resultados sugerem que a idade não altera significativamente a resistência de união do sistema adesivo à dentina. |
| first_indexed | 2024-12-23T11:39:13Z |
| format | Article |
| id | doaj.art-70e1f2d5c59b46d9852be54d0831421f |
| institution | Directory Open Access Journal |
| issn | 1678-7757 1678-7765 |
| language | English |
| last_indexed | 2024-12-23T11:39:13Z |
| publishDate | 2003-12-01 |
| publisher | University of São Paulo |
| record_format | Article |
| series | Journal of Applied Oral Science |
| spelling | doaj.art-70e1f2d5c59b46d9852be54d0831421f2022-12-21T17:48:32ZengUniversity of São PauloJournal of Applied Oral Science1678-77571678-77652003-12-0111434234710.1590/S1678-77572003000400013Effect of tooth age on bond strength to dentin Efeito da idade na resistência de uniãoMarcelo GianniniPatrícia ChavesMarcelo Tavares de OliveiraThis in vitro study evaluated the effect of tooth age on the tensile bond strength of Prime & Bond NT adhesive system to dentin. Human third molars from the five age groups were analyzed: A- 17 to 20yrs, B- 21 to 30yrs, C- 31 to 40yrs, D- 41 to 50yrs and E- 51 to 63yrs. The occlusal enamel was removed using a diamond saw under water cooling and the dentin surface was wet-ground with 600-grit SiC paper to obtain flat surfaces. The adhesive system was applied according to the manufacturer's instructions and a 6-mm high resin "crown" was built-up with resin composite. Teeth were stored for 24 hours in distilled water at 37ºC and prepared for micro-tensile testing. Each specimen was mounted in a testing jig attached to a universal testing machine and stressed in tension at a crosshead speed of 0.5mm/min until failure. The means of tensile bond strength were (MPa): A- 21.42 ± 7.52ª; B- 30.13 ± 10.19ª; C- 31.69 ± 11.78ª; D- 30.69 ± 8.47ª and E- 35.66 ± 9.54ª. No statistically significant difference was observed among the age groups (p > 0.05). The results suggested that the tensile bond strength of the adhesive system was not significantly affected by dentin aging.<br>Este estudo avaliou, in vitro, o efeito da idade na resistência à tração do sistema adesivo Prime & Bond NT no substrato dentinário. Foram utilizados terceiros molares humanos de cinco faixas etárias: A- 17 a 20, B- 21 a 30, C- 31 a 40, D- 41 a 50 e E- 51 a 63. O esmalte oclusal foi removido utilizando disco de diamante e a superfície dentinária abrasionada e planificada com lixa de SiC (600) sob refrigeração. O sistema adesivo foi aplicado de acordo com as recomendações do fabricante e um bloco de resina composta de 6 mm de altura foi confeccionado na superfície dentinária. Os dentes foram armazenados em água por 24 horas a 37ºC e preparados para o ensaio de micro-tração. Cada espécime foi fixado no dispositivo de micro-tração que estava acoplado a uma máquina universal de ensaio e testado numa velocidade de 0,5 mm/min. As médias de resistência à tração foram (MPa): A- 21,42 ± 7,52ª; B- 30,13 ± 10,19ª; C- 31,69 ± 11,78ª; D- 30,69 ± 8,47ª e E- 35,66 ± 9,54ª. Nenhuma diferença significativa foi observada entre os grupos formados pelas faixas etárias (p > 0,05). Os resultados sugerem que a idade não altera significativamente a resistência de união do sistema adesivo à dentina.http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572003000400013DentinaIdadeSistema adesivoResistência de uniãoDentinTooth ageAdhesive systemBond strength |
| spellingShingle | Marcelo Giannini Patrícia Chaves Marcelo Tavares de Oliveira Effect of tooth age on bond strength to dentin Efeito da idade na resistência de união Journal of Applied Oral Science Dentina Idade Sistema adesivo Resistência de união Dentin Tooth age Adhesive system Bond strength |
| title | Effect of tooth age on bond strength to dentin Efeito da idade na resistência de união |
| title_full | Effect of tooth age on bond strength to dentin Efeito da idade na resistência de união |
| title_fullStr | Effect of tooth age on bond strength to dentin Efeito da idade na resistência de união |
| title_full_unstemmed | Effect of tooth age on bond strength to dentin Efeito da idade na resistência de união |
| title_short | Effect of tooth age on bond strength to dentin Efeito da idade na resistência de união |
| title_sort | effect of tooth age on bond strength to dentin efeito da idade na resistencia de uniao |
| topic | Dentina Idade Sistema adesivo Resistência de união Dentin Tooth age Adhesive system Bond strength |
| url | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572003000400013 |
| work_keys_str_mv | AT marcelogiannini effectoftoothageonbondstrengthtodentinefeitodaidadenaresistenciadeuniao AT patriciachaves effectoftoothageonbondstrengthtodentinefeitodaidadenaresistenciadeuniao AT marcelotavaresdeoliveira effectoftoothageonbondstrengthtodentinefeitodaidadenaresistenciadeuniao |