Effects of Natural Chitosan as Biopolymer Coupling Agent on the Pyrolysis Kinetics of Wood Flour/ Polyvinyl Chloride Composites
The thermal degradation behavior and pyrolysis kinetic models of wood flour (WF)/PVC composites before and after adding chitosan were studied using thermogravimetry (TGA) and nine common kinetic model functions (f(α)). The results indicated that the thermal degradation temperature of WF/PVC composit...
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
North Carolina State University
2015-06-01
|
| Series: | BioResources |
| Subjects: | |
| Online Access: | http://ojs.cnr.ncsu.edu/index.php/BioRes/article/view/BioRes_10_3_4903_Xu_Natural_Chitosan_Biopolymer_Coupling_Agent |
| Summary: | The thermal degradation behavior and pyrolysis kinetic models of wood flour (WF)/PVC composites before and after adding chitosan were studied using thermogravimetry (TGA) and nine common kinetic model functions (f(α)). The results indicated that the thermal degradation temperature of WF/PVC composites was delayed to a higher value after adding chitosan. The first-order reaction order (L1) model and second-order reaction order (L2) model were found to be the best reaction order functions for the description of mass loss kinetics of WF/PVC without chitosan during the first and second stages. Two L2 models were suitable for both degradation stages of WF/CS/PVC. Activation energy (E) and frequency factor (A) for WF/PVC and WF/CS/PVC corresponded to 26.05 kJ·mol-1, 4.08×103 s-1, and 40.89 kJ·mol-1, 2.11×1010 s-1 at the first degradation stage, respectively, and 97.83 kJ·mol-1, 1.11×107 s-1 and 92.88 kJ·mol-1, 1.56×1011 s-1 at the second degradation stage. |
|---|---|