STUDY ON ANTI-CRACKING PERFORMANCE EVALUATION METHOD OF STEEL FIBER REINFORCED CERAMSITE CONCRETE (SFRCC) BASED ON PARTLY-RESTRAINED SHRINKAGE RING
In the study of crack resistance of steel fiber reinforced concrete in steel fiber on concrete deformation ability and prevent the Angle of the micro cracks, and the lack of overall evaluation on the performance of steel fiber reinforced concrete crack. By tinder barrier-free restrain some experimen...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Czech Technical University, Prague
2017-12-01
|
| Series: | Civil Engineering Journal |
| Subjects: | |
| Online Access: | http://www.civilengineeringjournal.cz/archive/issues/2017/2017_4/4-2017-0033.pdf |
| _version_ | 1797711656354054144 |
|---|---|
| author | Zhang Yi-fan |
| author_facet | Zhang Yi-fan |
| author_sort | Zhang Yi-fan |
| collection | DOAJ |
| description | In the study of crack resistance of steel fiber reinforced concrete in steel fiber on concrete deformation ability and prevent the Angle of the micro cracks, and the lack of overall evaluation on the performance of steel fiber reinforced concrete crack. By tinder barrier-free restrain some experimental research on steel fiber ceramsite concrete shrinkage ring crack resistance, and use the test results within the definition of steel ring strain from expansion to contraction cut-off age for early and late ages, and the ages of the cut-off point for the early and the late steel fiber ceramsite concrete anti-cracking performance evaluation. The results show that the anti-cracking properties of the steel fiber ceramic concrete are improved with the increase of steel fiber content. |
| first_indexed | 2024-03-12T07:10:16Z |
| format | Article |
| id | doaj.art-76542669b81a4a86be3c8546d900adc2 |
| institution | Directory Open Access Journal |
| issn | 1805-2576 |
| language | English |
| last_indexed | 2024-03-12T07:10:16Z |
| publishDate | 2017-12-01 |
| publisher | Czech Technical University, Prague |
| record_format | Article |
| series | Civil Engineering Journal |
| spelling | doaj.art-76542669b81a4a86be3c8546d900adc22023-09-02T23:09:19ZengCzech Technical University, PragueCivil Engineering Journal1805-25762017-12-012017439440310.14311/CEJ.2017.04.0033STUDY ON ANTI-CRACKING PERFORMANCE EVALUATION METHOD OF STEEL FIBER REINFORCED CERAMSITE CONCRETE (SFRCC) BASED ON PARTLY-RESTRAINED SHRINKAGE RINGZhang Yi-fan0College of Environment and Civil Engineering,Chengdu University of Technology,Chengdu 610059, ChinaIn the study of crack resistance of steel fiber reinforced concrete in steel fiber on concrete deformation ability and prevent the Angle of the micro cracks, and the lack of overall evaluation on the performance of steel fiber reinforced concrete crack. By tinder barrier-free restrain some experimental research on steel fiber ceramsite concrete shrinkage ring crack resistance, and use the test results within the definition of steel ring strain from expansion to contraction cut-off age for early and late ages, and the ages of the cut-off point for the early and the late steel fiber ceramsite concrete anti-cracking performance evaluation. The results show that the anti-cracking properties of the steel fiber ceramic concrete are improved with the increase of steel fiber content.http://www.civilengineeringjournal.cz/archive/issues/2017/2017_4/4-2017-0033.pdfAlkali slag cementNo diaphragm shrinkage ringConcrete structureEvaluation of crack resistance |
| spellingShingle | Zhang Yi-fan STUDY ON ANTI-CRACKING PERFORMANCE EVALUATION METHOD OF STEEL FIBER REINFORCED CERAMSITE CONCRETE (SFRCC) BASED ON PARTLY-RESTRAINED SHRINKAGE RING Civil Engineering Journal Alkali slag cement No diaphragm shrinkage ring Concrete structure Evaluation of crack resistance |
| title | STUDY ON ANTI-CRACKING PERFORMANCE EVALUATION METHOD OF STEEL FIBER REINFORCED CERAMSITE CONCRETE (SFRCC) BASED ON PARTLY-RESTRAINED SHRINKAGE RING |
| title_full | STUDY ON ANTI-CRACKING PERFORMANCE EVALUATION METHOD OF STEEL FIBER REINFORCED CERAMSITE CONCRETE (SFRCC) BASED ON PARTLY-RESTRAINED SHRINKAGE RING |
| title_fullStr | STUDY ON ANTI-CRACKING PERFORMANCE EVALUATION METHOD OF STEEL FIBER REINFORCED CERAMSITE CONCRETE (SFRCC) BASED ON PARTLY-RESTRAINED SHRINKAGE RING |
| title_full_unstemmed | STUDY ON ANTI-CRACKING PERFORMANCE EVALUATION METHOD OF STEEL FIBER REINFORCED CERAMSITE CONCRETE (SFRCC) BASED ON PARTLY-RESTRAINED SHRINKAGE RING |
| title_short | STUDY ON ANTI-CRACKING PERFORMANCE EVALUATION METHOD OF STEEL FIBER REINFORCED CERAMSITE CONCRETE (SFRCC) BASED ON PARTLY-RESTRAINED SHRINKAGE RING |
| title_sort | study on anti cracking performance evaluation method of steel fiber reinforced ceramsite concrete sfrcc based on partly restrained shrinkage ring |
| topic | Alkali slag cement No diaphragm shrinkage ring Concrete structure Evaluation of crack resistance |
| url | http://www.civilengineeringjournal.cz/archive/issues/2017/2017_4/4-2017-0033.pdf |
| work_keys_str_mv | AT zhangyifan studyonanticrackingperformanceevaluationmethodofsteelfiberreinforcedceramsiteconcretesfrccbasedonpartlyrestrainedshrinkagering |