Silicon Carbide Precursor: Structure Analysis and Thermal Behavior from Polymer Cross-Linking to Pyrolyzed Ceramics
The Silres H62C methyl-phenyl-vinyl-hydrogen polysiloxane is a promising candidate as a SiC precursor for 3D printing based on photopolymerization reaction. An in-depth nuclear magnetic resonance spectroscopy analysis allowed us to determine its structure and quantify its functional groups. The poly...
Main Authors: | Sébastien Vry, Marilyne Roumanie, Pierre-Alain Bayle, Sébastien Rolère, Guillaume Bernard-Granger |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2022-11-01
|
Series: | Ceramics |
Subjects: | |
Online Access: | https://www.mdpi.com/2571-6131/5/4/76 |
Similar Items
-
Transmission Electron Microscopy Investigations on a Polysiloxane Preceramic Polymer Pyrolyzed at High Temperature in Argon
by: Sébastien Vry, et al.
Published: (2020-10-01) -
Decreasing Resistivity of Silicon Carbide Ceramics by Incorporation of Graphene
by: Ningning Cai, et al.
Published: (2020-08-01) -
Microstructure Evolution and Performance Improvement of Silicon Carbide Ceramics via Impregnation Method
by: Wei Li, et al.
Published: (2022-02-01) -
Effect of Bi-B-Si-Zn-Al glass additive on the properties of low-temperature sintered silicon carbide ceramics
by: Lan Zhang, et al.
Published: (2023-01-01) -
Study of The Gas-Swelling Mechanisms in Silicon Carbide Ceramics under High-Temperature Irradiation with Helium Ions
by: Kymbat M. Tynyshbayeva, et al.
Published: (2023-08-01)