Effect of Ca on microstructure and high temperature creep properties of AM60-1Ce alloy
A series of AM60-1Ce-xCa (x=0, 0.5, 1.5, 2.5) magnesium alloys were prepared by gravity casting method and analyzed by means of XRD, DSC and SEM. The effects of Ca on normal temperature mechanical properties and high temperature creep behavior of alloys were characterized by tensile and constant c...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Foundry Journal Agency
2019-03-01
|
| Series: | China Foundry |
| Subjects: | |
| Online Access: | http://ff.foundryworld.com/uploadfile/2019040233652393.pdf |
| Summary: | A series of AM60-1Ce-xCa (x=0, 0.5, 1.5, 2.5) magnesium alloys were prepared by gravity casting
method and analyzed by means of XRD, DSC and SEM. The effects of Ca on normal temperature mechanical
properties and high temperature creep behavior of alloys were characterized by tensile and constant creep test.
Microstructure analysis indicated that Ca was preferentially combined with Al in the alloy to form the high melting
point Al2Ca phase at the grain boundary. The addition of Ca can refine the crystal grains and reduces the content
of β-Mg17Al12 phase. With the increase of Ca content in the alloy, Al2Ca phases at the grain boundary gradually
changed to the network of lamellar structure, and replaced the β-Mg17Al12 phase as the main strengthening phase
gradually. The creep resistance of the alloy continuously increases because the high-temperature stable phase
Al2Ca firmly nailed at grain boundaries impedes the sliding of grain boundaries. However, when the addition of Ca
was more than 1.5%, mechanical properties of the alloy started to decrease, which was probably due to the large
amount of irregularly shaped Al2Ca phases at the grain boundary. Experimental results show that the optimal
addition amount of Ca is 1.5wt.%. |
|---|---|