Residual stress in TI6AL4V objects produced by direct metal laser sintering
Direct Metal Laser Sintering produces 3D objects using a layer-by- layer method in which powder is deposited in thin layers. Laser beam scans over the powder fusing powder particles as well as the previous layer. High-concentration of laser energy input leads to high thermal gradients which induce r...
| المؤلفون الرئيسيون: | , , |
|---|---|
| التنسيق: | مقال |
| اللغة: | English |
| منشور في: |
Stellenbosch University
2016-12-01
|
| سلاسل: | South African Journal of Industrial Engineering |
| الموضوعات: | |
| الوصول للمادة أونلاين: | http://sajie.journals.ac.za/pub/article/view/1468 |
| الملخص: | Direct Metal Laser Sintering produces 3D objects using a layer-by- layer method in which powder is deposited in thin layers. Laser beam scans over the powder fusing powder particles as well as the previous layer. High-concentration of laser energy input leads to high thermal gradients which induce residual stress within the as- built parts. Ti6Al4V (ELI) samples have been manufactured by EOSINT M280 system at prescribed by EOS process-parameters. Residual stresses were measured by XRD method. Microstructure, values and directions of principal stresses inTi6Al4V DMLS samples were analysed. |
|---|---|
| تدمد: | 1012-277X 2224-7890 |