Biomass-derived Activated Carbon for Rechargeable Lithium-Sulfur Batteries
High-surface-area activated carbon (HSAAC) was synthesized by carbonizing coconut shells and subsequently activating the material with KOH. The as-prepared HSAAC had a mostly microporous structure (with small mesoporous inclusions) and exhibited a high specific surface area of 2258.7 m2g-1 and an av...
| Main Authors: | , , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
North Carolina State University
2014-11-01
|
| Series: | BioResources |
| Subjects: | |
| Online Access: | http://ojs.cnr.ncsu.edu/index.php/BioRes/article/view/BioRes_10_1_155_Liu_Biomass_Carbon_Sulfur_Batteries |
| Summary: | High-surface-area activated carbon (HSAAC) was synthesized by carbonizing coconut shells and subsequently activating the material with KOH. The as-prepared HSAAC had a mostly microporous structure (with small mesoporous inclusions) and exhibited a high specific surface area of 2258.7 m2g-1 and an average pore size of 2.246 nm. Sulfur was then loaded into the activated carbon (AC), and this S/HSAAC (62 wt%) was used as a cathode for Li-S batteries. These batteries delivered an initial discharge capacity of 1233 mAhg-1 at a current density of 200 mAg-1. Due to the strong absorption force of the micropores and a high pore volume, the cells retained 929 mAhg-1 with 80% capacity retention of the initial discharge after 100 cycles. Considering its low cost and ability to be produced at a large-scale, biomass-derived HSAAC is a promising electrode material that may advance high-energy rechargeable lithium-sulfur batteries toward use in practical applications. |
|---|---|
| ISSN: | 1930-2126 1930-2126 |