Effect of counter body on wear behavior of plasma-sprayed TiO2-45Cr2O3 coating.
The aim of this study was to determine the counter body effect on the wear behavior of TiO2-45 Cr2O3 coating. The commercial TiO2-45 Cr2O3 coating powder was deposited onto the surface of the AISI 316 L substrate using the APS method. Dry sliding wear tests were performed with Al2O3 and WC-Co counte...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Taylor & Francis Group
2021-01-01
|
| Series: | Journal of Asian Ceramic Societies |
| Subjects: | |
| Online Access: | http://dx.doi.org/10.1080/21870764.2020.1863574 |
| _version_ | 1819199140220895232 |
|---|---|
| author | Yılmaz Küçük |
| author_facet | Yılmaz Küçük |
| author_sort | Yılmaz Küçük |
| collection | DOAJ |
| description | The aim of this study was to determine the counter body effect on the wear behavior of TiO2-45 Cr2O3 coating. The commercial TiO2-45 Cr2O3 coating powder was deposited onto the surface of the AISI 316 L substrate using the APS method. Dry sliding wear tests were performed with Al2O3 and WC-Co counter body balls under different loads (5 N, 10 N, and 15 N) and reciprocating frequencies (1 Hz, 2 Hz, and 3 Hz). The COF values obtained from the Al2O3 ball were found to be higher than that of the WC-Co ball. In general, increasing load and sliding speed caused higher wear volume values for both counter body balls. When using Al2O3 ball under the 5 N load, a higher amount of wear debris and crack formation was observed, whereas, for higher loads, a larger plastic deformation zone which has lots of pitting and spalling was determined. As for the WC-Co ball, swelling-induced spallation and delamination were recorded as the effective wear mechanisms as well as the plastic deformation. |
| first_indexed | 2024-12-23T03:11:36Z |
| format | Article |
| id | doaj.art-7c9d1f6b94e7472eaf1a332e3b78f1f6 |
| institution | Directory Open Access Journal |
| issn | 2187-0764 |
| language | English |
| last_indexed | 2024-12-23T03:11:36Z |
| publishDate | 2021-01-01 |
| publisher | Taylor & Francis Group |
| record_format | Article |
| series | Journal of Asian Ceramic Societies |
| spelling | doaj.art-7c9d1f6b94e7472eaf1a332e3b78f1f62022-12-21T18:02:14ZengTaylor & Francis GroupJournal of Asian Ceramic Societies2187-07642021-01-019123725210.1080/21870764.2020.18635741863574Effect of counter body on wear behavior of plasma-sprayed TiO2-45Cr2O3 coating.Yılmaz Küçük0Bartin UniversityThe aim of this study was to determine the counter body effect on the wear behavior of TiO2-45 Cr2O3 coating. The commercial TiO2-45 Cr2O3 coating powder was deposited onto the surface of the AISI 316 L substrate using the APS method. Dry sliding wear tests were performed with Al2O3 and WC-Co counter body balls under different loads (5 N, 10 N, and 15 N) and reciprocating frequencies (1 Hz, 2 Hz, and 3 Hz). The COF values obtained from the Al2O3 ball were found to be higher than that of the WC-Co ball. In general, increasing load and sliding speed caused higher wear volume values for both counter body balls. When using Al2O3 ball under the 5 N load, a higher amount of wear debris and crack formation was observed, whereas, for higher loads, a larger plastic deformation zone which has lots of pitting and spalling was determined. As for the WC-Co ball, swelling-induced spallation and delamination were recorded as the effective wear mechanisms as well as the plastic deformation.http://dx.doi.org/10.1080/21870764.2020.1863574apstio2-45 cr2o3 coatingdry sliding wearreciprocating test |
| spellingShingle | Yılmaz Küçük Effect of counter body on wear behavior of plasma-sprayed TiO2-45Cr2O3 coating. Journal of Asian Ceramic Societies aps tio2-45 cr2o3 coating dry sliding wear reciprocating test |
| title | Effect of counter body on wear behavior of plasma-sprayed TiO2-45Cr2O3 coating. |
| title_full | Effect of counter body on wear behavior of plasma-sprayed TiO2-45Cr2O3 coating. |
| title_fullStr | Effect of counter body on wear behavior of plasma-sprayed TiO2-45Cr2O3 coating. |
| title_full_unstemmed | Effect of counter body on wear behavior of plasma-sprayed TiO2-45Cr2O3 coating. |
| title_short | Effect of counter body on wear behavior of plasma-sprayed TiO2-45Cr2O3 coating. |
| title_sort | effect of counter body on wear behavior of plasma sprayed tio2 45cr2o3 coating |
| topic | aps tio2-45 cr2o3 coating dry sliding wear reciprocating test |
| url | http://dx.doi.org/10.1080/21870764.2020.1863574 |
| work_keys_str_mv | AT yılmazkucuk effectofcounterbodyonwearbehaviorofplasmasprayedtio245cr2o3coating |