| Summary: | This work reports yarn pull-out studies of commercially available Kevlar<sup>®</sup> KM2+ individual yarns coated with metallic layers (copper, aluminum, aluminum nitride and silver) via a directed vapor deposition process. The uncoated control and metal-coated Kevlar<sup>®</sup> yarns are hand-woven into fabric swatches for quasi-static pull-out experiments. To perform these experiments, a yarn pull-out fixture is custom-designed and fabricated to apply transverse pre-tension to the fabric. Three levels of transverse pre-tensions are studied at 100 N, 200 N, and 400 N. The results showed that both peak pull-out force and energy absorption during the pull-out process increase with increase in transverse pre-tension. All the metal-coated groups showed an approximately 200% increase in peak pull-out force and a 20% reduction in tenacity compared to uncoated control. Furthermore, all the metal-coated groups showed an increase in energy absorption, with aluminum-coated yarns showing the highest increase of 230% compared to control. These results suggest enhanced frictional interactions during yarn pull-out in metal-coated yarns compared to uncoated control as evidenced by the surface roughness profile of individual fibers and inter-yarn frictional calculations.
|
|---|