The production of hydroxyapatite prototypes from solid bodies of gypsum/polyvinyl alcohol composites
Prototypes of porous hydroxyapatite (HAp) were produced from Gypsum/PVA composite, using a mass proportion of 15% polymer. The material was obtained by means of chemical conversion in (NH4)2HPO4 0.5 mol.L-1 solution and NH4OH 6.0 mol.L-1 alkaline medium for pH control, maintained between 6.0 and 9.0...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Associação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol)
2014-05-01
|
| Series: | Materials Research |
| Subjects: | |
| Online Access: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392014000700008&tlng=en |
| Summary: | Prototypes of porous hydroxyapatite (HAp) were produced from Gypsum/PVA composite, using a mass proportion of 15% polymer. The material was obtained by means of chemical conversion in (NH4)2HPO4 0.5 mol.L-1 solution and NH4OH 6.0 mol.L-1 alkaline medium for pH control, maintained between 6.0 and 9.0. The reaction occurred at a temperature of 100ºC at different test times. The obtained HAp was characterized by several techniques, such as FTIR, which identified the SO4(2-) groups characteristic for the Gypsum block, and the PO4(3-) groups that are attributed to the biomaterial HAp, besides XRD and SEM, which made it possible to confirm a successful conversion of the material. Tests for mechanical resistance to compression (σc) were carried out for both materials as well. |
|---|---|
| ISSN: | 1516-1439 |