Self-assembled GaInNAs/GaAsN quantum dot lasers: solid source molecular beam epitaxy growth and high-temperature operation
<p>Abstract</p><p>Self-assembled GaInNAs quantum dots (QDs) were grown on GaAs (001) substrate using solid-source molecular-beam epitaxy (SSMBE) equipped with a radio-frequency nitrogen plasma source. The GaInNAs QD growth characteristics were extensively investigated using atomic-...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
SpringerOpen
2006-01-01
|
| Series: | Nanoscale Research Letters |
| Subjects: | |
| Online Access: | http://dx.doi.org/10.1007/s11671-006-9009-5 |
| Summary: | <p>Abstract</p><p>Self-assembled GaInNAs quantum dots (QDs) were grown on GaAs (001) substrate using solid-source molecular-beam epitaxy (SSMBE) equipped with a radio-frequency nitrogen plasma source. The GaInNAs QD growth characteristics were extensively investigated using atomic-force microscopy (AFM), photoluminescence (PL), and transmission electron microscopy (TEM) measurements. Self-assembled GaInNAs/GaAsN single layer QD lasers grown using SSMBE have been fabricated and characterized. The laser worked under continuous wave (CW) operation at room temperature (RT) with emission wavelength of 1175.86 nm. Temperature-dependent measurements have been carried out on the GaInNAs QD lasers. The lowest obtained threshold current density in this work is ∼1.05 kA/cm<sup>2</sup>from a GaInNAs QD laser (50 × 1,700 µm<sup>2</sup>) at 10 °C. High-temperature operation up to 65 °C was demonstrated from an unbonded GaInNAs QD laser (50 × 1,060 µm<sup>2</sup>), with high characteristic temperature of 79.4 K in the temperature range of 10–60 °C.</p> |
|---|---|
| ISSN: | 1931-7573 1556-276X |