SYNTHESIS OF NANO SIZED MESOPOROUS γ - Al2O3POWDER FROM DOMESTIC HAMEDAN KAOLIN
A method for producing high surface area nano-sized mesoporous alumina from inexpensive Iranian kaolin as raw material is proposed. In this method, first, kaolin was purified for purifying Kaolin, High Grade Magnetic Separation and leaching with HCl and chemical bleaching treatment by using sodium d...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Iran University of Science & Technology
2015-03-01
|
| Series: | Iranian Journal of Materials Science and Engineering |
| Subjects: | |
| Online Access: | http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-77&slc_lang=en&sid=1 |
| _version_ | 1818509133194723328 |
|---|---|
| author | Y. Kianinia A. K. Darban E. Taheri-Nassaj B. Rahnama A. Foroutan |
| author_facet | Y. Kianinia A. K. Darban E. Taheri-Nassaj B. Rahnama A. Foroutan |
| author_sort | Y. Kianinia |
| collection | DOAJ |
| description | A method for producing high surface area nano-sized mesoporous alumina from inexpensive Iranian kaolin
as raw material is proposed. In this method, first, kaolin was purified for purifying Kaolin, High Grade Magnetic
Separation and leaching with HCl and chemical bleaching treatment by using sodium dithionite (Na
2
S
2O4
) as reducing
agent in acidic media (H
2SO
4
) were used. Purified kaolin was calcined. After that, Al (hydr) oxide from acid -leachates of calcined kaolin was precipitated with ammonia, in presence of polyethylene glycol. Finally, a white
powder of nano-sized alumina particles was obtained after calcination. BET surface area, X-ray diffraction (XRD),
Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM) were used to characterize
the sample. The resulting alumina with relatively high surface area (201.53 m
2
g
-1
) and narrow mean pore diameter
(6.91 nm), consists of a particle size distribution ranging from 22 to 36 nm. |
| first_indexed | 2024-12-10T22:41:16Z |
| format | Article |
| id | doaj.art-8198f3a7ec3a4ed19dd0170052f8d0b0 |
| institution | Directory Open Access Journal |
| issn | 1735-0808 2383-3882 |
| language | English |
| last_indexed | 2024-12-10T22:41:16Z |
| publishDate | 2015-03-01 |
| publisher | Iran University of Science & Technology |
| record_format | Article |
| series | Iranian Journal of Materials Science and Engineering |
| spelling | doaj.art-8198f3a7ec3a4ed19dd0170052f8d0b02022-12-22T01:30:42ZengIran University of Science & TechnologyIranian Journal of Materials Science and Engineering1735-08082383-38822015-03-011215965SYNTHESIS OF NANO SIZED MESOPOROUS γ - Al2O3POWDER FROM DOMESTIC HAMEDAN KAOLINY. Kianinia0A. K. Darban1E. Taheri-Nassaj2B. Rahnama3A. Foroutan4 A method for producing high surface area nano-sized mesoporous alumina from inexpensive Iranian kaolin as raw material is proposed. In this method, first, kaolin was purified for purifying Kaolin, High Grade Magnetic Separation and leaching with HCl and chemical bleaching treatment by using sodium dithionite (Na 2 S 2O4 ) as reducing agent in acidic media (H 2SO 4 ) were used. Purified kaolin was calcined. After that, Al (hydr) oxide from acid -leachates of calcined kaolin was precipitated with ammonia, in presence of polyethylene glycol. Finally, a white powder of nano-sized alumina particles was obtained after calcination. BET surface area, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM) were used to characterize the sample. The resulting alumina with relatively high surface area (201.53 m 2 g -1 ) and narrow mean pore diameter (6.91 nm), consists of a particle size distribution ranging from 22 to 36 nm.http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-77&slc_lang=en&sid=1Nano- alumina kaolin Synthesis precipitation |
| spellingShingle | Y. Kianinia A. K. Darban E. Taheri-Nassaj B. Rahnama A. Foroutan SYNTHESIS OF NANO SIZED MESOPOROUS γ - Al2O3POWDER FROM DOMESTIC HAMEDAN KAOLIN Iranian Journal of Materials Science and Engineering Nano- alumina kaolin Synthesis precipitation |
| title | SYNTHESIS OF NANO SIZED MESOPOROUS γ - Al2O3POWDER FROM DOMESTIC HAMEDAN KAOLIN |
| title_full | SYNTHESIS OF NANO SIZED MESOPOROUS γ - Al2O3POWDER FROM DOMESTIC HAMEDAN KAOLIN |
| title_fullStr | SYNTHESIS OF NANO SIZED MESOPOROUS γ - Al2O3POWDER FROM DOMESTIC HAMEDAN KAOLIN |
| title_full_unstemmed | SYNTHESIS OF NANO SIZED MESOPOROUS γ - Al2O3POWDER FROM DOMESTIC HAMEDAN KAOLIN |
| title_short | SYNTHESIS OF NANO SIZED MESOPOROUS γ - Al2O3POWDER FROM DOMESTIC HAMEDAN KAOLIN |
| title_sort | synthesis of nano sized mesoporous γ al2o3powder from domestic hamedan kaolin |
| topic | Nano- alumina kaolin Synthesis precipitation |
| url | http://ijmse.iust.ac.ir/browse.php?a_code=A-10-127-77&slc_lang=en&sid=1 |
| work_keys_str_mv | AT ykianinia synthesisofnanosizedmesoporousgal2o3powderfromdomestichamedankaolin AT akdarban synthesisofnanosizedmesoporousgal2o3powderfromdomestichamedankaolin AT etaherinassaj synthesisofnanosizedmesoporousgal2o3powderfromdomestichamedankaolin AT brahnama synthesisofnanosizedmesoporousgal2o3powderfromdomestichamedankaolin AT aforoutan synthesisofnanosizedmesoporousgal2o3powderfromdomestichamedankaolin |