| Summary: | In this study, a reinforced geosynthetic cementitious composite mat (GCCM) with improved structural stability and reinforcement efficiency through yarn-in-lay technology was designed and manufactured. Additionally, a blowing agent was added to relax the cross-sectional reduction caused by the rapid curing and shrinkage for reduction of installation period. The impact resistance results showed a significant increase compared to the pre-reinforcement values. Through the analysis of blowing agent content, concrete filling ratio, and bending strength of the double raschel GCCM, optimal conditions were determined. Therefore, the double raschel GCCM showed improved flexural strength even after a short curing period of 10 days, along with excellent durability under environmental conditions.
|
|---|