Joining of Low-Carbon Steel Sheets with Al-Based Weld
The analysis of the connection steel/Al/steel made by resistance welding was performed. The used low-carbon steel had low content of carbon and other elements, aluminum was of 99.997 wt.% Al purity. Formation of various FeAl intermetallic phases found in the phase diagram depending on the duration o...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Polish Academy of Sciences
2016-03-01
|
| Series: | Archives of Metallurgy and Materials |
| Subjects: | |
| Online Access: | http://www.degruyter.com/view/j/amm.2016.61.issue-1/amm-2016-0012/amm-2016-0012.xml?format=INT |
| _version_ | 1819106851361390592 |
|---|---|
| author | Boczkal G. Perek-Nowak M. Majewska Z. |
| author_facet | Boczkal G. Perek-Nowak M. Majewska Z. |
| author_sort | Boczkal G. |
| collection | DOAJ |
| description | The analysis of the connection steel/Al/steel made by resistance welding was performed. The used low-carbon steel had low content of carbon and other elements, aluminum was of 99.997 wt.% Al purity. Formation of various FeAl intermetallic phases found in the phase diagram depending on the duration of the process was analyzed. Two distinctively different types of structure depending on time of welding were observed: 1) hypoeutectic structure for samples processed for 5 s, and 2) eutectic structure for samples processed for 10 s and more. The shear test showed increase of mechanical properties of the connection for the samples welded 10 s. |
| first_indexed | 2024-12-22T02:44:42Z |
| format | Article |
| id | doaj.art-869de9dcd65d40feb339075335e6b82b |
| institution | Directory Open Access Journal |
| issn | 2300-1909 |
| language | English |
| last_indexed | 2024-12-22T02:44:42Z |
| publishDate | 2016-03-01 |
| publisher | Polish Academy of Sciences |
| record_format | Article |
| series | Archives of Metallurgy and Materials |
| spelling | doaj.art-869de9dcd65d40feb339075335e6b82b2022-12-21T18:41:33ZengPolish Academy of SciencesArchives of Metallurgy and Materials2300-19092016-03-01611374210.1515/amm-2016-0012amm-2016-0012Joining of Low-Carbon Steel Sheets with Al-Based WeldBoczkal G.0Perek-Nowak M.1Majewska Z.2AGH University of Science and Technology, Faculty of Non-Ferrous Metals, al. Mickiewicza 30, 30-065 Krakow, PolandAGH University of Science and Technology, Faculty of Non-Ferrous Metals, al. Mickiewicza 30, 30-065 Krakow, PolandAGH University of Science and Technology, Faculty of Non-Ferrous Metals, al. Mickiewicza 30, 30-065 Krakow, PolandThe analysis of the connection steel/Al/steel made by resistance welding was performed. The used low-carbon steel had low content of carbon and other elements, aluminum was of 99.997 wt.% Al purity. Formation of various FeAl intermetallic phases found in the phase diagram depending on the duration of the process was analyzed. Two distinctively different types of structure depending on time of welding were observed: 1) hypoeutectic structure for samples processed for 5 s, and 2) eutectic structure for samples processed for 10 s and more. The shear test showed increase of mechanical properties of the connection for the samples welded 10 s.http://www.degruyter.com/view/j/amm.2016.61.issue-1/amm-2016-0012/amm-2016-0012.xml?format=INTresistance weldingAl/Fe interfaceshear test |
| spellingShingle | Boczkal G. Perek-Nowak M. Majewska Z. Joining of Low-Carbon Steel Sheets with Al-Based Weld Archives of Metallurgy and Materials resistance welding Al/Fe interface shear test |
| title | Joining of Low-Carbon Steel Sheets with Al-Based Weld |
| title_full | Joining of Low-Carbon Steel Sheets with Al-Based Weld |
| title_fullStr | Joining of Low-Carbon Steel Sheets with Al-Based Weld |
| title_full_unstemmed | Joining of Low-Carbon Steel Sheets with Al-Based Weld |
| title_short | Joining of Low-Carbon Steel Sheets with Al-Based Weld |
| title_sort | joining of low carbon steel sheets with al based weld |
| topic | resistance welding Al/Fe interface shear test |
| url | http://www.degruyter.com/view/j/amm.2016.61.issue-1/amm-2016-0012/amm-2016-0012.xml?format=INT |
| work_keys_str_mv | AT boczkalg joiningoflowcarbonsteelsheetswithalbasedweld AT pereknowakm joiningoflowcarbonsteelsheetswithalbasedweld AT majewskaz joiningoflowcarbonsteelsheetswithalbasedweld |