Avaliação do ciclo térmico de conformação por compressão de peças em poli(sulfeto de fenileno) reforçado com fibras contínuas de carbono Thermal cycles evaluation during the compression forming of parts made of polyphenylsulphide reinforced with continuous carbon fiber
Peças em compósito termoplástico PPS/Carbono foram conformadas com o processo de moldagem por compressão a quente utilizando três diferentes ciclos térmicos, que foram avaliados pela análise comparativa do material antes e após o processo de conformação. As caracterizações dos laminados, antes e apó...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Associação Brasileira de Polímeros
2008-03-01
|
| Series: | Polímeros |
| Subjects: | |
| Online Access: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0104-14282008000100016 |
| _version_ | 1818582777093685248 |
|---|---|
| author | Gustavo G. da Costa Edson C. Botelho Mirabel C. Rezende Michelle L. Costa |
| author_facet | Gustavo G. da Costa Edson C. Botelho Mirabel C. Rezende Michelle L. Costa |
| author_sort | Gustavo G. da Costa |
| collection | DOAJ |
| description | Peças em compósito termoplástico PPS/Carbono foram conformadas com o processo de moldagem por compressão a quente utilizando três diferentes ciclos térmicos, que foram avaliados pela análise comparativa do material antes e após o processo de conformação. As caracterizações dos laminados, antes e após a conformação, envolveram inspeção visual, análises por microscopia óptica avaliando a presença de vazios ou delaminações, determinação de cristalinidade pela técnica de DSC e avaliação das propriedades mecânicas em flexão. A análise dos resultados obtidos permite verificar que as peças conformadas não apresentam delaminações e vazios. Porém, no caso em que foi utilizado o molde mais frio (100 °C) verifica-se um decréscimo nas propriedades mecânicas de até 25% e uma diferença significativa do grau de cristalinidade medido na face da peça (13%) para o cerne da mesma (21%). Dado este não observado nas outras condições de processamento avaliadas (moldes a 170 e 210 °C), as quais apresentam graus de cristalinidade nas faces e no centro em torno de 20%.<br>Thermoplastic composite parts were produced by the hot press compression molding process with three different thermal cycles, which were evaluated employing the material comparative analysis, before and after the manufacturing of parts. The properties of laminates and parts were evaluated by visual inspection, presence of voids or delamination by using optical microscopy, degree of crystallinity (DoC) utilizing DSC technique and mechanical properties making use of the flexural test. The results showed no delamination or voids. However, when the coldest mold was used (100 °C), the mechanical properties decreased up to 25% and a significant difference of DoC was observed from the part surfaces in contact with the mold (13%) to its centre (21%). This did not occur with the other processing conditions (molds at 170 and 210 °C), which exhibited DoCs around 20%. |
| first_indexed | 2024-12-16T07:54:46Z |
| format | Article |
| id | doaj.art-86ad9146d1e94def968c9719d85dea93 |
| institution | Directory Open Access Journal |
| issn | 0104-1428 1678-5169 |
| language | English |
| last_indexed | 2024-12-16T07:54:46Z |
| publishDate | 2008-03-01 |
| publisher | Associação Brasileira de Polímeros |
| record_format | Article |
| series | Polímeros |
| spelling | doaj.art-86ad9146d1e94def968c9719d85dea932022-12-21T22:38:46ZengAssociação Brasileira de PolímerosPolímeros0104-14281678-51692008-03-01181818610.1590/S0104-14282008000100016Avaliação do ciclo térmico de conformação por compressão de peças em poli(sulfeto de fenileno) reforçado com fibras contínuas de carbono Thermal cycles evaluation during the compression forming of parts made of polyphenylsulphide reinforced with continuous carbon fiberGustavo G. da CostaEdson C. BotelhoMirabel C. RezendeMichelle L. CostaPeças em compósito termoplástico PPS/Carbono foram conformadas com o processo de moldagem por compressão a quente utilizando três diferentes ciclos térmicos, que foram avaliados pela análise comparativa do material antes e após o processo de conformação. As caracterizações dos laminados, antes e após a conformação, envolveram inspeção visual, análises por microscopia óptica avaliando a presença de vazios ou delaminações, determinação de cristalinidade pela técnica de DSC e avaliação das propriedades mecânicas em flexão. A análise dos resultados obtidos permite verificar que as peças conformadas não apresentam delaminações e vazios. Porém, no caso em que foi utilizado o molde mais frio (100 °C) verifica-se um decréscimo nas propriedades mecânicas de até 25% e uma diferença significativa do grau de cristalinidade medido na face da peça (13%) para o cerne da mesma (21%). Dado este não observado nas outras condições de processamento avaliadas (moldes a 170 e 210 °C), as quais apresentam graus de cristalinidade nas faces e no centro em torno de 20%.<br>Thermoplastic composite parts were produced by the hot press compression molding process with three different thermal cycles, which were evaluated employing the material comparative analysis, before and after the manufacturing of parts. The properties of laminates and parts were evaluated by visual inspection, presence of voids or delamination by using optical microscopy, degree of crystallinity (DoC) utilizing DSC technique and mechanical properties making use of the flexural test. The results showed no delamination or voids. However, when the coldest mold was used (100 °C), the mechanical properties decreased up to 25% and a significant difference of DoC was observed from the part surfaces in contact with the mold (13%) to its centre (21%). This did not occur with the other processing conditions (molds at 170 and 210 °C), which exhibited DoCs around 20%.http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0104-14282008000100016Compósito termoplásticopoli(sulfeto de fenileno)PPSconformação por moldagem a quentegrau de cristalinidadeThermoplastic compositepolyphenylene sulphidePPShot press compression moldingdegree of crystallinity |
| spellingShingle | Gustavo G. da Costa Edson C. Botelho Mirabel C. Rezende Michelle L. Costa Avaliação do ciclo térmico de conformação por compressão de peças em poli(sulfeto de fenileno) reforçado com fibras contínuas de carbono Thermal cycles evaluation during the compression forming of parts made of polyphenylsulphide reinforced with continuous carbon fiber Polímeros Compósito termoplástico poli(sulfeto de fenileno) PPS conformação por moldagem a quente grau de cristalinidade Thermoplastic composite polyphenylene sulphide PPS hot press compression molding degree of crystallinity |
| title | Avaliação do ciclo térmico de conformação por compressão de peças em poli(sulfeto de fenileno) reforçado com fibras contínuas de carbono Thermal cycles evaluation during the compression forming of parts made of polyphenylsulphide reinforced with continuous carbon fiber |
| title_full | Avaliação do ciclo térmico de conformação por compressão de peças em poli(sulfeto de fenileno) reforçado com fibras contínuas de carbono Thermal cycles evaluation during the compression forming of parts made of polyphenylsulphide reinforced with continuous carbon fiber |
| title_fullStr | Avaliação do ciclo térmico de conformação por compressão de peças em poli(sulfeto de fenileno) reforçado com fibras contínuas de carbono Thermal cycles evaluation during the compression forming of parts made of polyphenylsulphide reinforced with continuous carbon fiber |
| title_full_unstemmed | Avaliação do ciclo térmico de conformação por compressão de peças em poli(sulfeto de fenileno) reforçado com fibras contínuas de carbono Thermal cycles evaluation during the compression forming of parts made of polyphenylsulphide reinforced with continuous carbon fiber |
| title_short | Avaliação do ciclo térmico de conformação por compressão de peças em poli(sulfeto de fenileno) reforçado com fibras contínuas de carbono Thermal cycles evaluation during the compression forming of parts made of polyphenylsulphide reinforced with continuous carbon fiber |
| title_sort | avaliacao do ciclo termico de conformacao por compressao de pecas em poli sulfeto de fenileno reforcado com fibras continuas de carbono thermal cycles evaluation during the compression forming of parts made of polyphenylsulphide reinforced with continuous carbon fiber |
| topic | Compósito termoplástico poli(sulfeto de fenileno) PPS conformação por moldagem a quente grau de cristalinidade Thermoplastic composite polyphenylene sulphide PPS hot press compression molding degree of crystallinity |
| url | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0104-14282008000100016 |
| work_keys_str_mv | AT gustavogdacosta avaliacaodociclotermicodeconformacaoporcompressaodepecasempolisulfetodefenilenoreforcadocomfibrascontinuasdecarbonothermalcyclesevaluationduringthecompressionformingofpartsmadeofpolyphenylsulphidereinforcedwithcontinuouscarbonfiber AT edsoncbotelho avaliacaodociclotermicodeconformacaoporcompressaodepecasempolisulfetodefenilenoreforcadocomfibrascontinuasdecarbonothermalcyclesevaluationduringthecompressionformingofpartsmadeofpolyphenylsulphidereinforcedwithcontinuouscarbonfiber AT mirabelcrezende avaliacaodociclotermicodeconformacaoporcompressaodepecasempolisulfetodefenilenoreforcadocomfibrascontinuasdecarbonothermalcyclesevaluationduringthecompressionformingofpartsmadeofpolyphenylsulphidereinforcedwithcontinuouscarbonfiber AT michellelcosta avaliacaodociclotermicodeconformacaoporcompressaodepecasempolisulfetodefenilenoreforcadocomfibrascontinuasdecarbonothermalcyclesevaluationduringthecompressionformingofpartsmadeofpolyphenylsulphidereinforcedwithcontinuouscarbonfiber |