Self-organization processes in nanopowder dispersed system based on zirconia under pressure action
The work is devoted to the studying of mechanisms of zirconia nanoparticles growth (enlargement) in temperature region were diffusion processes isn’t beginning. A comparative analysis of morphology of compacted using high hydrostatic pressure ZrO2 + 3 mol% Y2O3 nanopowders (YSZ, particle size 9 nm)...
| Main Authors: | , , , , , , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2020-03-01
|
| Series: | Results in Physics |
| Subjects: | |
| Online Access: | http://www.sciencedirect.com/science/article/pii/S2211379719305583 |
| _version_ | 1811340031707578368 |
|---|---|
| author | A.S. Doroshkevich A.V. Shylo V.A. Glazunova G.K. Volkova A.K. Kirillov T. Yu. Zelenyak V.V. Burkhovetskiy V.A. Turchenko V.S. Doroshkevich A.A. Nabiyev T.A. Vasylenko A. Kh. Islamov M.L. Craus |
| author_facet | A.S. Doroshkevich A.V. Shylo V.A. Glazunova G.K. Volkova A.K. Kirillov T. Yu. Zelenyak V.V. Burkhovetskiy V.A. Turchenko V.S. Doroshkevich A.A. Nabiyev T.A. Vasylenko A. Kh. Islamov M.L. Craus |
| author_sort | A.S. Doroshkevich |
| collection | DOAJ |
| description | The work is devoted to the studying of mechanisms of zirconia nanoparticles growth (enlargement) in temperature region were diffusion processes isn’t beginning. A comparative analysis of morphology of compacted using high hydrostatic pressure ZrO2 + 3 mol% Y2O3 nanopowders (YSZ, particle size 9 nm) with different content of adsorbed moisture was conducted. The fact of granulation on a microscopic size scale of initially uniformly distributed dispersed phase with adsorbed water content of 11.5% was established. The results were considered by using thermodynamic principles of nanosized dispersed systems self-organization. The different precursors and external pressure was considered as a critical factor in the destabilization of the self-organization process at room temperature.It was shown that the observed effect is a form of manifestation of coagulation process in the studied dispersed system at room temperature range which is hidden under normal pressure. Conclusion about coagulation nature of growth process of ZrO2 nanoparticles at temperature range where thermal diffusion is still missing was done. The suggestion that widespread models of low-temperature growth of nanoparticles based on collective effects (orientation growth), which is suggest the orienting action of crystalline environment fields as a thermodynamic stimulus of growth processes, are a particular cases of manifestation of the overall coagulation process. |
| first_indexed | 2024-04-13T18:35:17Z |
| format | Article |
| id | doaj.art-87289025b2a94697ad32fb62db2ac8b3 |
| institution | Directory Open Access Journal |
| issn | 2211-3797 |
| language | English |
| last_indexed | 2024-04-13T18:35:17Z |
| publishDate | 2020-03-01 |
| publisher | Elsevier |
| record_format | Article |
| series | Results in Physics |
| spelling | doaj.art-87289025b2a94697ad32fb62db2ac8b32022-12-22T02:34:54ZengElsevierResults in Physics2211-37972020-03-0116102809Self-organization processes in nanopowder dispersed system based on zirconia under pressure actionA.S. Doroshkevich0A.V. Shylo1V.A. Glazunova2G.K. Volkova3A.K. Kirillov4T. Yu. Zelenyak5V.V. Burkhovetskiy6V.A. Turchenko7V.S. Doroshkevich8A.A. Nabiyev9T.A. Vasylenko10A. Kh. Islamov11M.L. Craus12Joint Institute for Nuclear Research, str. Joliot-Curie, 6, 141980 Dubna, Russian Federation; Donetsk Institute for Physics and Engineering named after O.O. Galkin NAS of Ukraine, Ukraine; Corresponding author at: Joint Institute for Nuclear Research, str. Joliot-Curie, 6, 141980 Dubna, Russian Federation.Donetsk Institute for Physics and Engineering named after O.O. Galkin NAS of Ukraine, UkraineDonetsk Institute for Physics and Engineering named after O.O. Galkin NAS of Ukraine, UkraineDonetsk Institute for Physics and Engineering named after O.O. Galkin NAS of Ukraine, UkraineInstitute for Physics of Mining Processes NAS of Ukraine, 83114, UkraineJoint Institute for Nuclear Research, str. Joliot-Curie, 6, 141980 Dubna, Russian FederationDonetsk Institute for Physics and Engineering named after O.O. Galkin NAS of Ukraine, UkraineJoint Institute for Nuclear Research, str. Joliot-Curie, 6, 141980 Dubna, Russian FederationDonetsk National University, Department of Biochemistry, str. Schorsa, 17a, Donetsk 83000, UkraineJoint Institute for Nuclear Research, str. Joliot-Curie, 6, 141980 Dubna, Russian Federation; ANAS Institute of Radiation Problems, 9 B. Vahabzade str., AZ1143 Baku, AzerbaijanInstitute for Physics of Mining Processes NAS of Ukraine, 83114, UkraineJoint Institute for Nuclear Research, str. Joliot-Curie, 6, 141980 Dubna, Russian FederationJoint Institute for Nuclear Research, str. Joliot-Curie, 6, 141980 Dubna, Russian FederationThe work is devoted to the studying of mechanisms of zirconia nanoparticles growth (enlargement) in temperature region were diffusion processes isn’t beginning. A comparative analysis of morphology of compacted using high hydrostatic pressure ZrO2 + 3 mol% Y2O3 nanopowders (YSZ, particle size 9 nm) with different content of adsorbed moisture was conducted. The fact of granulation on a microscopic size scale of initially uniformly distributed dispersed phase with adsorbed water content of 11.5% was established. The results were considered by using thermodynamic principles of nanosized dispersed systems self-organization. The different precursors and external pressure was considered as a critical factor in the destabilization of the self-organization process at room temperature.It was shown that the observed effect is a form of manifestation of coagulation process in the studied dispersed system at room temperature range which is hidden under normal pressure. Conclusion about coagulation nature of growth process of ZrO2 nanoparticles at temperature range where thermal diffusion is still missing was done. The suggestion that widespread models of low-temperature growth of nanoparticles based on collective effects (orientation growth), which is suggest the orienting action of crystalline environment fields as a thermodynamic stimulus of growth processes, are a particular cases of manifestation of the overall coagulation process.http://www.sciencedirect.com/science/article/pii/S2211379719305583Nanopowder dispersed systemsZirconiaLow temperature oxide nanoparticles growthElectron microscopy |
| spellingShingle | A.S. Doroshkevich A.V. Shylo V.A. Glazunova G.K. Volkova A.K. Kirillov T. Yu. Zelenyak V.V. Burkhovetskiy V.A. Turchenko V.S. Doroshkevich A.A. Nabiyev T.A. Vasylenko A. Kh. Islamov M.L. Craus Self-organization processes in nanopowder dispersed system based on zirconia under pressure action Results in Physics Nanopowder dispersed systems Zirconia Low temperature oxide nanoparticles growth Electron microscopy |
| title | Self-organization processes in nanopowder dispersed system based on zirconia under pressure action |
| title_full | Self-organization processes in nanopowder dispersed system based on zirconia under pressure action |
| title_fullStr | Self-organization processes in nanopowder dispersed system based on zirconia under pressure action |
| title_full_unstemmed | Self-organization processes in nanopowder dispersed system based on zirconia under pressure action |
| title_short | Self-organization processes in nanopowder dispersed system based on zirconia under pressure action |
| title_sort | self organization processes in nanopowder dispersed system based on zirconia under pressure action |
| topic | Nanopowder dispersed systems Zirconia Low temperature oxide nanoparticles growth Electron microscopy |
| url | http://www.sciencedirect.com/science/article/pii/S2211379719305583 |
| work_keys_str_mv | AT asdoroshkevich selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT avshylo selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT vaglazunova selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT gkvolkova selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT akkirillov selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT tyuzelenyak selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT vvburkhovetskiy selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT vaturchenko selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT vsdoroshkevich selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT aanabiyev selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT tavasylenko selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT akhislamov selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction AT mlcraus selforganizationprocessesinnanopowderdispersedsystembasedonzirconiaunderpressureaction |