Effect of Hot Rolling on Structure and Mechanical Properties of Mg–Y–Zn–Mn Alloys
The effect of hot rolling on the structure and mechanical properties of three Mg–Y–Zn–Mn alloys was studied depending on the process temperature and the reduction ratio. The original plates of cast WZM111, WZM211, and WZM321 alloys after heat treatment were subjected to rolling from an initial thick...
| Main Authors: | , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2023-01-01
|
| Series: | Metals |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2075-4701/13/2/223 |
| _version_ | 1797619315437993984 |
|---|---|
| author | Stanislav O. Rogachev Viacheslav E. Bazhenov Alexander A. Komissarov Anna V. Li Denis V. Ten Viacheslav V. Yushchuk Alexey Yu. Drobyshev Kwang Seon Shin |
| author_facet | Stanislav O. Rogachev Viacheslav E. Bazhenov Alexander A. Komissarov Anna V. Li Denis V. Ten Viacheslav V. Yushchuk Alexey Yu. Drobyshev Kwang Seon Shin |
| author_sort | Stanislav O. Rogachev |
| collection | DOAJ |
| description | The effect of hot rolling on the structure and mechanical properties of three Mg–Y–Zn–Mn alloys was studied depending on the process temperature and the reduction ratio. The original plates of cast WZM111, WZM211, and WZM321 alloys after heat treatment were subjected to rolling from an initial thickness of 7 mm to a final thickness of 0.2 mm at two temperatures, namely 400 and 450 °C. Optical and scanning electron microscopy, the microhardness measurement, and tensile testing were used to characterize the material. The rolling regimes that provide a good balance between the strength and ductility of the alloys were established. |
| first_indexed | 2024-03-11T08:25:17Z |
| format | Article |
| id | doaj.art-872e138a3ed84dc7ba20deec59049049 |
| institution | Directory Open Access Journal |
| issn | 2075-4701 |
| language | English |
| last_indexed | 2024-03-11T08:25:17Z |
| publishDate | 2023-01-01 |
| publisher | MDPI AG |
| record_format | Article |
| series | Metals |
| spelling | doaj.art-872e138a3ed84dc7ba20deec590490492023-11-16T22:06:23ZengMDPI AGMetals2075-47012023-01-0113222310.3390/met13020223Effect of Hot Rolling on Structure and Mechanical Properties of Mg–Y–Zn–Mn AlloysStanislav O. Rogachev0Viacheslav E. Bazhenov1Alexander A. Komissarov2Anna V. Li3Denis V. Ten4Viacheslav V. Yushchuk5Alexey Yu. Drobyshev6Kwang Seon Shin7Department of Physical Metallurgy and Physics of Strength, National University of Science and Technology MISiS, 119049 Moscow, RussiaCasting Department, National University of Science and Technology MISiS, 119049 Moscow, RussiaDepartment of Physical Metallurgy and Physics of Strength, National University of Science and Technology MISiS, 119049 Moscow, RussiaDepartment of Physical Metallurgy and Physics of Strength, National University of Science and Technology MISiS, 119049 Moscow, RussiaDepartment of Physical Metallurgy and Physics of Strength, National University of Science and Technology MISiS, 119049 Moscow, RussiaDepartment of Physical Metallurgy and Physics of Strength, National University of Science and Technology MISiS, 119049 Moscow, RussiaLaboratory of Medical Bioresorption and Bioresistance, Moscow State University of Medicine and Dentistry, 127473 Moscow, RussiaLaboratory of Medical Bioresorption and Bioresistance, Moscow State University of Medicine and Dentistry, 127473 Moscow, RussiaThe effect of hot rolling on the structure and mechanical properties of three Mg–Y–Zn–Mn alloys was studied depending on the process temperature and the reduction ratio. The original plates of cast WZM111, WZM211, and WZM321 alloys after heat treatment were subjected to rolling from an initial thickness of 7 mm to a final thickness of 0.2 mm at two temperatures, namely 400 and 450 °C. Optical and scanning electron microscopy, the microhardness measurement, and tensile testing were used to characterize the material. The rolling regimes that provide a good balance between the strength and ductility of the alloys were established.https://www.mdpi.com/2075-4701/13/2/223Mg–Y–Zn–Mn magnesium alloysrollingmechanical propertiesmicrostructure |
| spellingShingle | Stanislav O. Rogachev Viacheslav E. Bazhenov Alexander A. Komissarov Anna V. Li Denis V. Ten Viacheslav V. Yushchuk Alexey Yu. Drobyshev Kwang Seon Shin Effect of Hot Rolling on Structure and Mechanical Properties of Mg–Y–Zn–Mn Alloys Metals Mg–Y–Zn–Mn magnesium alloys rolling mechanical properties microstructure |
| title | Effect of Hot Rolling on Structure and Mechanical Properties of Mg–Y–Zn–Mn Alloys |
| title_full | Effect of Hot Rolling on Structure and Mechanical Properties of Mg–Y–Zn–Mn Alloys |
| title_fullStr | Effect of Hot Rolling on Structure and Mechanical Properties of Mg–Y–Zn–Mn Alloys |
| title_full_unstemmed | Effect of Hot Rolling on Structure and Mechanical Properties of Mg–Y–Zn–Mn Alloys |
| title_short | Effect of Hot Rolling on Structure and Mechanical Properties of Mg–Y–Zn–Mn Alloys |
| title_sort | effect of hot rolling on structure and mechanical properties of mg y zn mn alloys |
| topic | Mg–Y–Zn–Mn magnesium alloys rolling mechanical properties microstructure |
| url | https://www.mdpi.com/2075-4701/13/2/223 |
| work_keys_str_mv | AT stanislavorogachev effectofhotrollingonstructureandmechanicalpropertiesofmgyznmnalloys AT viacheslavebazhenov effectofhotrollingonstructureandmechanicalpropertiesofmgyznmnalloys AT alexanderakomissarov effectofhotrollingonstructureandmechanicalpropertiesofmgyznmnalloys AT annavli effectofhotrollingonstructureandmechanicalpropertiesofmgyznmnalloys AT denisvten effectofhotrollingonstructureandmechanicalpropertiesofmgyznmnalloys AT viacheslavvyushchuk effectofhotrollingonstructureandmechanicalpropertiesofmgyznmnalloys AT alexeyyudrobyshev effectofhotrollingonstructureandmechanicalpropertiesofmgyznmnalloys AT kwangseonshin effectofhotrollingonstructureandmechanicalpropertiesofmgyznmnalloys |