Investigation of corrosion properties of box boring din 20MnCr5 steel bars
In this study, boriding process was carried out on Ø11 mm diameter DIN 20MnCr5 quality steel bars, used in chain elements such as links and rings, and fasteners such as bolts, at 950oC boronizing temperature, boriding times of 2.5 and 7.5 hours. In this study, the formation and growth of the boride...
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
EDP Sciences
2023-01-01
|
| Series: | E3S Web of Conferences |
| Online Access: | https://www.e3s-conferences.org/articles/e3sconf/pdf/2023/38/e3sconf_conmechydro23_05035.pdf |
| _version_ | 1797775836010512384 |
|---|---|
| author | Şahin Nurullah Işikgül Aysun Ziyamukhamedova Umida Ahlatci Hayrettin Acarer Mustafa Sevim Mucahit |
| author_facet | Şahin Nurullah Işikgül Aysun Ziyamukhamedova Umida Ahlatci Hayrettin Acarer Mustafa Sevim Mucahit |
| author_sort | Şahin Nurullah |
| collection | DOAJ |
| description | In this study, boriding process was carried out on Ø11 mm diameter DIN 20MnCr5 quality steel bars, used in chain elements such as links and rings, and fasteners such as bolts, at 950oC boronizing temperature, boriding times of 2.5 and 7.5 hours. In this study, the formation and growth of the boride layer and the metallographic structure, the coating thickness and corrosion properties of the boronized steels were investigated depending on the boriding conditions. In the box boriding process, Ekabor-II powder mixture, with its commercial name, was used as boriding powder. According to the optical microstructure results made as a result of box boriding, the coating thickness was 371.5 μm in the Ø11 mm diameter boronized DIN 20MnCr5 steel bar for 7.5 hours boriding times while it was 195.6 ?m in that steel bar for 2.5 hours boriding times. Corrosion experiments were carried out in solutions prepared by adding 3.5% NaCl to distilled water. According to the results of the immersion test, the lowest corrosion rate in mdd was measured as 112 mg/(dm2 × day) in the Ø11 mm diameter, 7.5 hour boronized sample, and the highest corrosion rate in mdd was 1456.75 mg/(dm2 × day) in the untreated Ø11mm diameter sample. In the potentiodynamic polarization test, parallel results were obtained for immersion corrosion. Corrosion rate values (icor) were measured at the highest value of 209 × 10−6 A/cm2 in the untreated Ø11 diameter sample, while the lowest icor value was 0.0039 × 10−6 A/cm2 in the Ø11 mm diameter sample borided for 7.5 hours. |
| first_indexed | 2024-03-12T22:41:27Z |
| format | Article |
| id | doaj.art-882dd350ee56428ea15669594a31673d |
| institution | Directory Open Access Journal |
| issn | 2267-1242 |
| language | English |
| last_indexed | 2024-03-12T22:41:27Z |
| publishDate | 2023-01-01 |
| publisher | EDP Sciences |
| record_format | Article |
| series | E3S Web of Conferences |
| spelling | doaj.art-882dd350ee56428ea15669594a31673d2023-07-21T09:35:26ZengEDP SciencesE3S Web of Conferences2267-12422023-01-014010503510.1051/e3sconf/202340105035e3sconf_conmechydro23_05035Investigation of corrosion properties of box boring din 20MnCr5 steel barsŞahin Nurullah0Işikgül Aysun1Ziyamukhamedova Umida2Ahlatci Hayrettin3Acarer Mustafa4Sevim Mucahit5Karabuk UniversityKardemir Iron And Steel Factory Inc.Co.Tashkent State Transport UniversityKarabuk UniversitySelçuk UniversityKardemir Iron And Steel Factory Inc.Co.In this study, boriding process was carried out on Ø11 mm diameter DIN 20MnCr5 quality steel bars, used in chain elements such as links and rings, and fasteners such as bolts, at 950oC boronizing temperature, boriding times of 2.5 and 7.5 hours. In this study, the formation and growth of the boride layer and the metallographic structure, the coating thickness and corrosion properties of the boronized steels were investigated depending on the boriding conditions. In the box boriding process, Ekabor-II powder mixture, with its commercial name, was used as boriding powder. According to the optical microstructure results made as a result of box boriding, the coating thickness was 371.5 μm in the Ø11 mm diameter boronized DIN 20MnCr5 steel bar for 7.5 hours boriding times while it was 195.6 ?m in that steel bar for 2.5 hours boriding times. Corrosion experiments were carried out in solutions prepared by adding 3.5% NaCl to distilled water. According to the results of the immersion test, the lowest corrosion rate in mdd was measured as 112 mg/(dm2 × day) in the Ø11 mm diameter, 7.5 hour boronized sample, and the highest corrosion rate in mdd was 1456.75 mg/(dm2 × day) in the untreated Ø11mm diameter sample. In the potentiodynamic polarization test, parallel results were obtained for immersion corrosion. Corrosion rate values (icor) were measured at the highest value of 209 × 10−6 A/cm2 in the untreated Ø11 diameter sample, while the lowest icor value was 0.0039 × 10−6 A/cm2 in the Ø11 mm diameter sample borided for 7.5 hours.https://www.e3s-conferences.org/articles/e3sconf/pdf/2023/38/e3sconf_conmechydro23_05035.pdf |
| spellingShingle | Şahin Nurullah Işikgül Aysun Ziyamukhamedova Umida Ahlatci Hayrettin Acarer Mustafa Sevim Mucahit Investigation of corrosion properties of box boring din 20MnCr5 steel bars E3S Web of Conferences |
| title | Investigation of corrosion properties of box boring din 20MnCr5 steel bars |
| title_full | Investigation of corrosion properties of box boring din 20MnCr5 steel bars |
| title_fullStr | Investigation of corrosion properties of box boring din 20MnCr5 steel bars |
| title_full_unstemmed | Investigation of corrosion properties of box boring din 20MnCr5 steel bars |
| title_short | Investigation of corrosion properties of box boring din 20MnCr5 steel bars |
| title_sort | investigation of corrosion properties of box boring din 20mncr5 steel bars |
| url | https://www.e3s-conferences.org/articles/e3sconf/pdf/2023/38/e3sconf_conmechydro23_05035.pdf |
| work_keys_str_mv | AT sahinnurullah investigationofcorrosionpropertiesofboxboringdin20mncr5steelbars AT isikgulaysun investigationofcorrosionpropertiesofboxboringdin20mncr5steelbars AT ziyamukhamedovaumida investigationofcorrosionpropertiesofboxboringdin20mncr5steelbars AT ahlatcihayrettin investigationofcorrosionpropertiesofboxboringdin20mncr5steelbars AT acarermustafa investigationofcorrosionpropertiesofboxboringdin20mncr5steelbars AT sevimmucahit investigationofcorrosionpropertiesofboxboringdin20mncr5steelbars |