Synthesis, microstructural characterization, mechanical, fractographic and wear behavior of micro B4C particles reinforced Al2618 alloy aerospace composites
In the current studies an investigations were made to know the effect of 63 micron sized B4C particles addition on the mechanical and wear behavior of aerospace alloy Al2618 metal composites. Al2618 alloy with different weight percentages (2, 4, 6 and 8 wt. %) of 63 micron sized B4C particles reinfo...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gruppo Italiano Frattura
2022-10-01
|
| Series: | Fracture and Structural Integrity |
| Subjects: | |
| Online Access: | https://www.fracturae.com/index.php/fis/article/view/3572/3678 |
| _version_ | 1826903904480133120 |
|---|---|
| author | G. Veeresha B. Manjunatha V. Bharath Madeva Nagaral V. Auradi |
| author_facet | G. Veeresha B. Manjunatha V. Bharath Madeva Nagaral V. Auradi |
| author_sort | G. Veeresha |
| collection | DOAJ |
| description | In the current studies an investigations were made to know the effect of 63 micron sized B4C particles addition on the mechanical and wear behavior of aerospace alloy Al2618 metal composites. Al2618 alloy with different weight percentages (2, 4, 6 and 8 wt. %) of 63 micron sized B4C particles reinforced composites were produced by stir cast process. These synthesized composites were tested for various mechanical properties like hardness, compression strength and tensile behavior along with density measurements. Further, microstructural characterization was carried by SEM/EDS and XRD analysis to know the micron sized particles distribution and phases. Wear behavior of Al2618 alloy with 2 to 8 wt. % of B4C composites were studied as per ASTM G99 standards with varying loads and sliding speeds. By adding 63 micron sized B4C particles hardness, compression and tensile strength of Al2618 alloy was enriched with slight decrease in elongation. Further, wear resistance of Al2618 alloy was enriched with the accumulation of B4C particles. As load and speed on the specimen increased, there was increase in wear of Al2618 alloy and its composites. Various tensile fracture surface morphology and worn surface behavior was observed by SEM analysis |
| first_indexed | 2024-04-11T14:25:40Z |
| format | Article |
| id | doaj.art-89b93a75e8024f34b5ed9193da72c718 |
| institution | Directory Open Access Journal |
| issn | 1971-8993 |
| language | English |
| last_indexed | 2025-02-17T08:02:47Z |
| publishDate | 2022-10-01 |
| publisher | Gruppo Italiano Frattura |
| record_format | Article |
| series | Fracture and Structural Integrity |
| spelling | doaj.art-89b93a75e8024f34b5ed9193da72c7182025-01-03T00:39:12ZengGruppo Italiano FratturaFracture and Structural Integrity1971-89932022-10-01166238540710.3221/IGF-ESIS.62.2710.3221/IGF-ESIS.62.27Synthesis, microstructural characterization, mechanical, fractographic and wear behavior of micro B4C particles reinforced Al2618 alloy aerospace compositesG. VeereshaB. ManjunathaV. BharathMadeva NagaralV. AuradiIn the current studies an investigations were made to know the effect of 63 micron sized B4C particles addition on the mechanical and wear behavior of aerospace alloy Al2618 metal composites. Al2618 alloy with different weight percentages (2, 4, 6 and 8 wt. %) of 63 micron sized B4C particles reinforced composites were produced by stir cast process. These synthesized composites were tested for various mechanical properties like hardness, compression strength and tensile behavior along with density measurements. Further, microstructural characterization was carried by SEM/EDS and XRD analysis to know the micron sized particles distribution and phases. Wear behavior of Al2618 alloy with 2 to 8 wt. % of B4C composites were studied as per ASTM G99 standards with varying loads and sliding speeds. By adding 63 micron sized B4C particles hardness, compression and tensile strength of Al2618 alloy was enriched with slight decrease in elongation. Further, wear resistance of Al2618 alloy was enriched with the accumulation of B4C particles. As load and speed on the specimen increased, there was increase in wear of Al2618 alloy and its composites. Various tensile fracture surface morphology and worn surface behavior was observed by SEM analysishttps://www.fracturae.com/index.php/fis/article/view/3572/3678al2618 alloyb4cmicrostructuremechanical and wear propertiesfractographyworn morphology |
| spellingShingle | G. Veeresha B. Manjunatha V. Bharath Madeva Nagaral V. Auradi Synthesis, microstructural characterization, mechanical, fractographic and wear behavior of micro B4C particles reinforced Al2618 alloy aerospace composites Fracture and Structural Integrity al2618 alloy b4c microstructure mechanical and wear properties fractography worn morphology |
| title | Synthesis, microstructural characterization, mechanical, fractographic and wear behavior of micro B4C particles reinforced Al2618 alloy aerospace composites |
| title_full | Synthesis, microstructural characterization, mechanical, fractographic and wear behavior of micro B4C particles reinforced Al2618 alloy aerospace composites |
| title_fullStr | Synthesis, microstructural characterization, mechanical, fractographic and wear behavior of micro B4C particles reinforced Al2618 alloy aerospace composites |
| title_full_unstemmed | Synthesis, microstructural characterization, mechanical, fractographic and wear behavior of micro B4C particles reinforced Al2618 alloy aerospace composites |
| title_short | Synthesis, microstructural characterization, mechanical, fractographic and wear behavior of micro B4C particles reinforced Al2618 alloy aerospace composites |
| title_sort | synthesis microstructural characterization mechanical fractographic and wear behavior of micro b4c particles reinforced al2618 alloy aerospace composites |
| topic | al2618 alloy b4c microstructure mechanical and wear properties fractography worn morphology |
| url | https://www.fracturae.com/index.php/fis/article/view/3572/3678 |
| work_keys_str_mv | AT gveeresha synthesismicrostructuralcharacterizationmechanicalfractographicandwearbehaviorofmicrob4cparticlesreinforcedal2618alloyaerospacecomposites AT bmanjunatha synthesismicrostructuralcharacterizationmechanicalfractographicandwearbehaviorofmicrob4cparticlesreinforcedal2618alloyaerospacecomposites AT vbharath synthesismicrostructuralcharacterizationmechanicalfractographicandwearbehaviorofmicrob4cparticlesreinforcedal2618alloyaerospacecomposites AT madevanagaral synthesismicrostructuralcharacterizationmechanicalfractographicandwearbehaviorofmicrob4cparticlesreinforcedal2618alloyaerospacecomposites AT vauradi synthesismicrostructuralcharacterizationmechanicalfractographicandwearbehaviorofmicrob4cparticlesreinforcedal2618alloyaerospacecomposites |