| Summary: | In this study, single-spherical nanoscale zero valent iron (nZVI) particles with large specific sur-face area were successfully synthesized by a simple and rapid chemical reduction method. The XRD spectra and SEM–EDS images showed that the synthesized nZVI had excellent crystal struc-ture, but oxidation products, such as γ-Fe<sub>2</sub>O<sub>3</sub> and Fe<sub>3</sub>O<sub>4</sub>, were formed on the surface of the parti-cles. The effect of different factors on the removal of Cr(VI) by nZVI were studied, and the opti-mum experimental conditions were found. Kinetic and thermodynamic equations at different temperatures showed that the removal of Cr(VI) by nZVI was a single-layer chemical adsorption, conforming to pseudo-second-order kinetics. By applying the intraparticle diffusion model, the ad-sorption process was composed of three stages, namely rapid diffusion, chemical reduction, and in-ternal saturation. Mechanism analysis demonstrated that the removal of Cr(VI) by nZVI in-volved adsorption, reduction, precipitation and coprecipitation. Meanwhile, Cr(VI) was reduced to Cr(III) by nZVI, while FeCr<sub>2</sub>O<sub>4</sub>, Cr<sub>x</sub>Fe<sub>1−x</sub>OOH, and Cr<sub>x</sub>Fe<sub>1−x</sub>(OH)<sub>3</sub> were formed as end products. In addition, the study found that ascorbic acid, starch, and Cu modified nZVI can promote the removal efficiency of Cr(VI) in varying degrees due to the enhanced mobility of the particles. These results can provide new insights into the removal mechanisms of Cr(VI) by nZVI.
|
|---|