Effect of Oil – Corrosion on Tensile and Fatigue S-N Curve Properties of AA6061-T6
The present study described the effect of shot peening on mechanical properties and rotating corrosion –fatigue behavior (strength and life) of AA6061-T6. Ultimate tensile strength (UTS) and yield stress (YS) were reduced by 4.6% and 1.24% when immersing the tensile samples in crude oil for 60 days....
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Unviversity of Technology- Iraq
2021-03-01
|
| Series: | Engineering and Technology Journal |
| Subjects: | |
| Online Access: | https://etj.uotechnology.edu.iq/article_168121_6fda358f26f149b2827c398c398d332b.pdf |
| _version_ | 1797336444260319232 |
|---|---|
| author | Hussain J.M. Al-Alkawi Ghgada A. Aziz Shmoos R. Mazel |
| author_facet | Hussain J.M. Al-Alkawi Ghgada A. Aziz Shmoos R. Mazel |
| author_sort | Hussain J.M. Al-Alkawi |
| collection | DOAJ |
| description | The present study described the effect of shot peening on mechanical properties and rotating corrosion –fatigue behavior (strength and life) of AA6061-T6. Ultimate tensile strength (UTS) and yield stress (YS) were reduced by 4.6% and 1.24% when immersing the tensile samples in crude oil for 60 days. The values of (UTS) and (YS) were raised from 307 to 316 MPa and from 248 to 254 MPa respectively when treated for 10 min. shot peening (SP). Hardness of oil corrosion samples dropped due to pitting corrosion and slightly raised for SP prior to corrosion samples. Oil corrosion reduced the fatigue strength by (-1.25%). This percentage was enhanced due to SP to 2.377%. SP significantly increased the rotating fatigue life by a factor of 1.19 and 1.3 at (UTS) and (Ys) loads respectively. (SP) technique improved corrosion-fatigue resistance due to producing compressive residual stresses at surface layers. |
| first_indexed | 2024-03-08T08:54:33Z |
| format | Article |
| id | doaj.art-8aeff1ef41a94e56a43694390f6b721b |
| institution | Directory Open Access Journal |
| issn | 1681-6900 2412-0758 |
| language | English |
| last_indexed | 2024-03-08T08:54:33Z |
| publishDate | 2021-03-01 |
| publisher | Unviversity of Technology- Iraq |
| record_format | Article |
| series | Engineering and Technology Journal |
| spelling | doaj.art-8aeff1ef41a94e56a43694390f6b721b2024-02-01T07:17:29ZengUnviversity of Technology- IraqEngineering and Technology Journal1681-69002412-07582021-03-01393A40741410.30684/etj.v39i3A.298168121Effect of Oil – Corrosion on Tensile and Fatigue S-N Curve Properties of AA6061-T6Hussain J.M. Al-Alkawi0Ghgada A. Aziz1Shmoos R. Mazel2Electro-mechanical Eng. Dept., University of Technology, Baghdad, Iraq. Alalkawi2012@yahoo.comElectro-mechanical Eng. Dept., University of Technology, Baghdad, Iraq. ghadasama@yahoo.comElectro-mechanical Eng. Dept., University of Technology, Baghdad, Iraq. shmoos_rahem@yahoo.comThe present study described the effect of shot peening on mechanical properties and rotating corrosion –fatigue behavior (strength and life) of AA6061-T6. Ultimate tensile strength (UTS) and yield stress (YS) were reduced by 4.6% and 1.24% when immersing the tensile samples in crude oil for 60 days. The values of (UTS) and (YS) were raised from 307 to 316 MPa and from 248 to 254 MPa respectively when treated for 10 min. shot peening (SP). Hardness of oil corrosion samples dropped due to pitting corrosion and slightly raised for SP prior to corrosion samples. Oil corrosion reduced the fatigue strength by (-1.25%). This percentage was enhanced due to SP to 2.377%. SP significantly increased the rotating fatigue life by a factor of 1.19 and 1.3 at (UTS) and (Ys) loads respectively. (SP) technique improved corrosion-fatigue resistance due to producing compressive residual stresses at surface layers.https://etj.uotechnology.edu.iq/article_168121_6fda358f26f149b2827c398c398d332b.pdfaa6061-t6mechanical propertieshardnessfatigueoil corrosionshot peening |
| spellingShingle | Hussain J.M. Al-Alkawi Ghgada A. Aziz Shmoos R. Mazel Effect of Oil – Corrosion on Tensile and Fatigue S-N Curve Properties of AA6061-T6 Engineering and Technology Journal aa6061-t6 mechanical properties hardness fatigue oil corrosion shot peening |
| title | Effect of Oil – Corrosion on Tensile and Fatigue S-N Curve Properties of AA6061-T6 |
| title_full | Effect of Oil – Corrosion on Tensile and Fatigue S-N Curve Properties of AA6061-T6 |
| title_fullStr | Effect of Oil – Corrosion on Tensile and Fatigue S-N Curve Properties of AA6061-T6 |
| title_full_unstemmed | Effect of Oil – Corrosion on Tensile and Fatigue S-N Curve Properties of AA6061-T6 |
| title_short | Effect of Oil – Corrosion on Tensile and Fatigue S-N Curve Properties of AA6061-T6 |
| title_sort | effect of oil corrosion on tensile and fatigue s n curve properties of aa6061 t6 |
| topic | aa6061-t6 mechanical properties hardness fatigue oil corrosion shot peening |
| url | https://etj.uotechnology.edu.iq/article_168121_6fda358f26f149b2827c398c398d332b.pdf |
| work_keys_str_mv | AT hussainjmalalkawi effectofoilcorrosionontensileandfatiguesncurvepropertiesofaa6061t6 AT ghgadaaaziz effectofoilcorrosionontensileandfatiguesncurvepropertiesofaa6061t6 AT shmoosrmazel effectofoilcorrosionontensileandfatiguesncurvepropertiesofaa6061t6 |