Microstructure Evolution of Mg-Sn-Y Alloy Solidified under High Pressure and Temperature Gradient
The microstructures of Mg-1Sn-2.5Y (wt%) alloys solidified under high pressures were investigated. In addition, a mathematical model was established to analyze the effects of solidification pressure and cooling rate on the average grain size. The results show that the alloy was solidified under high...
Main Authors: | Chunming Zou, Rong Zhang, Zunjie Wei, Hongwei Wang |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2022-01-01
|
Series: | Crystals |
Subjects: | |
Online Access: | https://www.mdpi.com/2073-4352/12/2/149 |
Similar Items
-
Influence of Solidification Parameters on the Amount of Eutectic and Secondary Arm Spacing of Al–7wt% Si Alloy Solidified under Microgravity
by: András Roósz, et al.
Published: (2022-03-01) -
Modeling Dendrite Coarsening and Remelting during Directional Solidification of Al-06wt.%Cu Alloy
by: Ibrahim Sari, et al.
Published: (2024-02-01) -
Effect of Growth Rate on Coarsening of Secondary Dendrite Arm Spacings in Directionally Solidified of Al-8.8La-1.2Ni Ternary Alloy
by: Erkan Üstün, et al.
Published: (2022-08-01) -
Modelling of the Solidifying Microstructure of Inconel 718: Quasi-Binary Approximation
by: Nikolai Kropotin, et al.
Published: (2023-06-01) -
The Role of Dilute Solute Additions on Growth Restriction in Cu-, Al-, Mg- and Ti-Based Alloys
by: Maria J. Balart, et al.
Published: (2022-09-01)