Study of surface defects and crystallinity of MWCNTs growth in FCCVD
This research investigated the structural growth of multiwalled carbon nanotubes (MWCNTs) in a double stage horizontal chemical vapor deposition (CVD) reactor. Ethylene was used as a carbon source for nucleation of nanotubes. Ferrocene catalyst weight was varied from 0.1 to 0.2 g to demonstrate the...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
De Gruyter
2017-11-01
|
| Series: | Science and Engineering of Composite Materials |
| Subjects: | |
| Online Access: | https://doi.org/10.1515/secm-2014-0253 |
| Summary: | This research investigated the structural growth of multiwalled carbon nanotubes (MWCNTs) in a double stage horizontal chemical vapor deposition (CVD) reactor. Ethylene was used as a carbon source for nucleation of nanotubes. Ferrocene catalyst weight was varied from 0.1 to 0.2 g to demonstrate the growth of MWCNTs on Si/SiO2/Al2O3 substrate. The obtained data revealed that the weight of the catalyst significantly affects the diameter, crystallinity, alignment and yield of the nanotubes. Lower inner-shell spacing and the ratio of D-Raman peak intensity and G-Raman peak intensity (ID/IG ratio) were obtained with 0.15 g of ferrocene, which was an indication of relatively pure carbon nanotubes (CNTs) growth. Raman spectra also confirmed the highly crystalline and relatively pure CNTs structures with ID/IG ratio of 0.700. TGA data revealed the formation of 97% pure nanotubes with oxidation temperature of 620°C. However, above and below the optimum (0.15 g of ferrocene), some of the grown CNTs were found defective and few black spots were also seen in TEM micrographs. |
|---|---|
| ISSN: | 0792-1233 2191-0359 |