| Summary: | The main goal of this work was to evaluate the thermal insulation and sound absorption properties of open-cell rigid polyurethane foams synthesized with different contents of cooking oil-based polyol. The content of the applied bio-polyol as well as flame retardant (triethyl phosphate) in the foam formulation had a significant influence on the cellular structures of the materials. The open-cell polyurethane foams were characterized by apparent densities in the range 16–30 kg/m<sup>3</sup>. The sound absorption coefficients of the polyurethanes with various contents of bio-polyol were determined using the standing wave method (Kundt’s tube) in the frequency range of 100–6300 Hz. The effect of the content of the bio-polyol and flame retardant on the coefficient of thermal conductivity (at average temperatures of 0, 10 and 20 °C) as well as the compressive strength (at 20 and −10 °C) was analyzed. Different trends were observed in terms of the thermal insulation properties and sound absorption ability of the open-cell polyurethanes due to the addition of bio-polyol. In conclusion, it is necessary to use systems containing both petrochemical and bio-based raw materials.
|
|---|