Characterization of Nb2O5-Ni Coating Prepared by DC Sputtering
The Nb2O5-Ni coating was processed using DC sputtering on structural steel and study characterization of composite coating SEM/EDS inspection indicated clearly perfect incorporation of Nb2O5 within the nickel rich. Increasing in surface roughness and decreasing in average diameters of particles were...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Unviversity of Technology- Iraq
2021-04-01
|
| Series: | Engineering and Technology Journal |
| Subjects: | |
| Online Access: | https://etj.uotechnology.edu.iq/article_168135_a2bd2d4c3503563f2d086664cd64caba.pdf |
| _version_ | 1827366712379441152 |
|---|---|
| author | Hiyam M. Jedy Rana A. Anaee Abdullah A. Abdulkarim |
| author_facet | Hiyam M. Jedy Rana A. Anaee Abdullah A. Abdulkarim |
| author_sort | Hiyam M. Jedy |
| collection | DOAJ |
| description | The Nb2O5-Ni coating was processed using DC sputtering on structural steel and study characterization of composite coating SEM/EDS inspection indicated clearly perfect incorporation of Nb2O5 within the nickel rich. Increasing in surface roughness and decreasing in average diameters of particles were obtained for coated surface compared with uncoated surface from AFM analysis, in addition, microhardness test and thickness test showed that increasing of the hardness value to 163 HV for Nb2O5 - Ni composite coating compared to 132 HV for uncoated samples, the hardness for Ni coating also increasing to155 HV and the thickness for Nb2O5-Ni composite coatings increased significantly compared to uncoated samples. |
| first_indexed | 2024-03-08T08:54:36Z |
| format | Article |
| id | doaj.art-9697a8770dcb427e858c77fcb1910bf5 |
| institution | Directory Open Access Journal |
| issn | 1681-6900 2412-0758 |
| language | English |
| last_indexed | 2024-03-08T08:54:36Z |
| publishDate | 2021-04-01 |
| publisher | Unviversity of Technology- Iraq |
| record_format | Article |
| series | Engineering and Technology Journal |
| spelling | doaj.art-9697a8770dcb427e858c77fcb1910bf52024-02-01T07:17:37ZengUnviversity of Technology- IraqEngineering and Technology Journal1681-69002412-07582021-04-01394A56557210.30684/etj.v39i4A.1902168135Characterization of Nb2O5-Ni Coating Prepared by DC SputteringHiyam M. Jedy0Rana A. Anaee1Abdullah A. Abdulkarim2Material Engineering Department, University of Technology, Baghdad, Iraq, hoyamhimi123@gmail.comMaterial Engineering Department, University of Technology, Baghdad, Iraq,130033@uotechnology.edu.iqMinistry of Industry and Minerals, Baghdad, Iraq masterchem76@yahoo.comThe Nb2O5-Ni coating was processed using DC sputtering on structural steel and study characterization of composite coating SEM/EDS inspection indicated clearly perfect incorporation of Nb2O5 within the nickel rich. Increasing in surface roughness and decreasing in average diameters of particles were obtained for coated surface compared with uncoated surface from AFM analysis, in addition, microhardness test and thickness test showed that increasing of the hardness value to 163 HV for Nb2O5 - Ni composite coating compared to 132 HV for uncoated samples, the hardness for Ni coating also increasing to155 HV and the thickness for Nb2O5-Ni composite coatings increased significantly compared to uncoated samples.https://etj.uotechnology.edu.iq/article_168135_a2bd2d4c3503563f2d086664cd64caba.pdfnb2o5-ni coatingdc sputteringsemedsmicrohardness |
| spellingShingle | Hiyam M. Jedy Rana A. Anaee Abdullah A. Abdulkarim Characterization of Nb2O5-Ni Coating Prepared by DC Sputtering Engineering and Technology Journal nb2o5-ni coating dc sputtering sem eds microhardness |
| title | Characterization of Nb2O5-Ni Coating Prepared by DC Sputtering |
| title_full | Characterization of Nb2O5-Ni Coating Prepared by DC Sputtering |
| title_fullStr | Characterization of Nb2O5-Ni Coating Prepared by DC Sputtering |
| title_full_unstemmed | Characterization of Nb2O5-Ni Coating Prepared by DC Sputtering |
| title_short | Characterization of Nb2O5-Ni Coating Prepared by DC Sputtering |
| title_sort | characterization of nb2o5 ni coating prepared by dc sputtering |
| topic | nb2o5-ni coating dc sputtering sem eds microhardness |
| url | https://etj.uotechnology.edu.iq/article_168135_a2bd2d4c3503563f2d086664cd64caba.pdf |
| work_keys_str_mv | AT hiyammjedy characterizationofnb2o5nicoatingpreparedbydcsputtering AT ranaaanaee characterizationofnb2o5nicoatingpreparedbydcsputtering AT abdullahaabdulkarim characterizationofnb2o5nicoatingpreparedbydcsputtering |