TRANSPARENT SUPERHYDROPHILIC SiO2/TiO2/SiO2 TRI-LAYER NANOSTRUCTURED ANTIFOGGING THIN FILM
SiO2/TiO2/SiO2 thin films were deposited on glass substrates using an electron beam physical vapor deposition technique. The structure, morphology, surface composition, surface roughness, optical properties, and hydrophilic properties of the thin film were investigated. The structure measurement sho...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of Chemistry and Technology, Prague
2013-09-01
|
| Series: | Ceramics-Silikáty |
| Subjects: | |
| Online Access: | http://www.ceramics-silikaty.cz/2013/pdf/2013_03_210.pdf |
| Summary: | SiO2/TiO2/SiO2 thin films were deposited on glass substrates using an electron beam physical vapor deposition technique. The structure, morphology, surface composition, surface roughness, optical properties, and hydrophilic properties of the thin film were investigated. The structure measurement shows that only anatase phase was exhibited in the thin film. In the TiO2 thin film, the crystals nucleated from the thin films was homogeneous and the average crystalline sizes were 35 nm. The transmittance spectra of the films revealed transparency in the visible region of the spectrum. SiO2/TiO2/SiO2 thin film showed better hydrophilicity under irradiation and storage in comparison to SiO2/TiO2 thin film. SiO2/TiO2/SiO2 tri-layer thin film showed superhydrophilicity which greatly encourages the antifogging function of the film. |
|---|---|
| ISSN: | 0862-5468 1804-5847 |