Weld Formation Mechanism and Microstructural Evolution of TC4/304 Stainless Steel Joint with Cu-Based Filler Wire and Preheating
Ti-Fe intermetallic compounds were effectively suppressed with Cu-based filler wire and weld formation was greatly improved with the preheating of substrates when joining TC4 titanium alloy and 304 stainless steel. A Ti/Cu transition zone consisting of complex TiCu, Ti<sub>2</sub>Cu<s...