Weld Formation Mechanism and Microstructural Evolution of TC4/304 Stainless Steel Joint with Cu-Based Filler Wire and Preheating
Ti-Fe intermetallic compounds were effectively suppressed with Cu-based filler wire and weld formation was greatly improved with the preheating of substrates when joining TC4 titanium alloy and 304 stainless steel. A Ti/Cu transition zone consisting of complex TiCu, Ti<sub>2</sub>Cu<s...
Main Authors: | Junzhao Li, Yibo Liu, Zuyang Zhen, Peng Jin, Qingjie Sun, Jicai Feng |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2019-09-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/12/19/3071 |
Similar Items
-
Contact reactive brazing of TC4/304 stainless steel dissimilar metals by interrupted arc pulsed welding
by: Yanqiu Li, et al.
Published: (2023-09-01) -
COLD ROLLING ORTHODONTIC WIRES OF AUSTENITIC STAINLESS STEEL AISI 304
by: Rodrigo Santos Messner, et al.
Published: (2013-03-01) -
Study on microstructure and properties of TA1-304 stainless steel explosive welding cladding plate
by: Lu Liangyu, et al.
Published: (2020-01-01) -
The Effects of TIG Welding Rod Compositions on Microstructural and Mechanical Properties of Dissimilar AISI 304L and 420 Stainless Steel Welds
by: Aziz Barış Başyiğit, et al.
Published: (2018-11-01) -
Effect of drawing and annealing on the microstructure and mechanical properties of 304 austenitic stainless steel wire
by: Qinhua Xu, et al.
Published: (2021-01-01)