Effect of Service-Induced Degradation on Residual Stress Rupture Life of a Directionally Solidified Superalloy
The influence of service-induced degradation on residual life is very important for the safe service of turbine blades. In this study, a series of simulation experiments were conducted on a directionally solidified superalloy under (880–1020) °C/(70–220) MPa and interrupted after 500 h. Then, the st...