| Summary: | Metal oxide photocatalyst is a promising wastewater treatment process due to its simplicity, high efficiency, and low cost, as well as being environmentally friendly and non-energy consuming. The perovskite structure material, SrTi1−xNbxO3 (STNO) with x = 0, 0.01, 0.03, and 0.05, was successfully synthesized by the sol-gel auto-combustion method. Samples with a pure phase and cubic perovskite structure were obtained. The Rietveld refinement results showed that the lattice parameter and unit cell density increased as the Nb-doping level increased. The particle size of the STNO decreases with increasing Nb doping content. Photoluminescence was excited at 327 nm, producing violet, green, and blue emissions, while the Nb content asserts an insignificant effect on the bandgap (Eg). The Nyquist plot and Mott-Schottky analysis were used to determine the photoelectrode performance of the STNO samples. The photocatalytic activity of STNO on the decolorization of methylene blue (MB) under UV irradiation increased with increasing Nb content and optimization at x = 0.05, corresponding to the results obtained from photoluminescence, Eg, Nyquist plot, and Mott-Schottky analyses.
|
|---|