Low-Temperature Impact Fracture Behavior of Medium Manganese Steel with Bcc-fcc Duplex Microstructures
Impact fracture behavior at low temperatures was investigated in medium manganese steel with bcc-fcc duplex microstructures. The impact energy was above 150 J (−80~20 °C) and the fractography showed dimples for inter-critical annealing at 630 °C (QHA) because of the high retained austenite stability...
| Main Authors: | , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2024-02-01
|
| Series: | Metals |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2075-4701/14/3/293 |
| Summary: | Impact fracture behavior at low temperatures was investigated in medium manganese steel with bcc-fcc duplex microstructures. The impact energy was above 150 J (−80~20 °C) and the fractography showed dimples for inter-critical annealing at 630 °C (QHA) because of the high retained austenite stability and low martensite dislocation density. The impact energy was from 180 J (20 °C) to 60 J (−80 °C) and the fractography was intergranular for inter-critical annealing at 610 °C (QLA) because of the low stability of RA and carbides precipitated at the prior austenite grain boundaries. The impact energy was below 60 J (−80~20 °C) and the fractography showed cleavage for direct quenching (DQ) because of the high dislocation density of martensite. |
|---|---|
| ISSN: | 2075-4701 |