| Summary: | This paper describes in detail a series of static tests conducted in a three-point bend configuration on three build orientations (i.e., 0°, 45°, and 90°) of additively manufactured Nylon 12 (PA12) specimens produced with a powder refresh ratio of 50%, using a benchtop industrial SLS platform, Formlabs Fuse 1. The bending strength and flexural elasticity moduli are determined following ISO 173 specifications and by employing a more complex equation that considers the influence of large deflections as per ISO 14125 indications. Statistical variability of experimental data is considered and compared to the results from the literature. Through a fractographic SEM study, the damage morphologies of tested specimens are analyzed and associated with the recorded load-deflection curves for an accurate perception of build orientation-dependent anisotropy in bending properties of AM PA12 SLS specimens. A surprising result of this investigation is that the specimens built with 45° orientation showed superior modulus elasticity in flexure but a low bending strength compared to flatwise oriented specimens. In addition, a Weibull reliability quantification of bending strength is adapted to pinpoint the effects of internal 3D printing flaws (contained within a characteristic highly-stressed volume of material) over the failure probability of the three build orientations in question.
|
|---|