Microstructure and Mechanical Properties of Stainless Steel/6082 Aluminum Alloy Heterogeneous Laser Welded Joint
The microstructures and mechanical properties of laser penetration welded joints of overlap steel-on-aluminum were investigated. The structure of the intermetallic compound layer without interlayer consists of FeAl and FeAl<sub>3</sub> phases. After the Ni-foil was added, the thickness o...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2023-10-01
|
| Series: | Materials |
| Subjects: | |
| Online Access: | https://www.mdpi.com/1996-1944/16/21/6958 |
| Summary: | The microstructures and mechanical properties of laser penetration welded joints of overlap steel-on-aluminum were investigated. The structure of the intermetallic compound layer without interlayer consists of FeAl and FeAl<sub>3</sub> phases. After the Ni-foil was added, the thickness of the intermetallic compound layer and the content of the brittle and hard Al-Fe phase decreased significantly, and some new phases of Al<sub>0.9</sub>Ni<sub>1.1</sub> and FeNi were formed. It was found that the Ni interlayer enhanced the tensile property of the joint by about 40% and decreased the microhardness of the intermetallic compounds, which is attributed to the improvement of the toughness of the welded joint made by the Ni interlayer. It is an effective way to improve the mechanical properties of the laser welding joint by adding a nickel interlayer to improve the metallurgical reaction. |
|---|---|
| ISSN: | 1996-1944 |