Sodium-Vanadium Bronze Na<sub>9</sub>V<sub>14</sub>O<sub>35</sub>: An Electrode Material for Na-Ion Batteries
Na<sub>9</sub>V<sub>14</sub>O<sub>35</sub> (η-Na<sub>x</sub>V<sub>2</sub>O<sub>5</sub>) has been synthesized via solid-state reaction in an evacuated sealed silica ampoule and tested as electroactive material for Na-ion batterie...
Main Authors: | Maria A. Kirsanova, Alexey S. Akmaev, Mikhail V. Gorbunov, Daria Mikhailova, Artem M. Abakumov |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2021-12-01
|
Series: | Molecules |
Subjects: | |
Online Access: | https://www.mdpi.com/1420-3049/27/1/86 |
Similar Items
-
Structural and Electrochemical Properties of Layered P2-Na<sub>0.8</sub>Co<sub>0.8</sub>Ti<sub>0.2</sub>O<sub>2</sub> Cathode in Sodium-Ion Batteries
by: Björn Pohle, et al.
Published: (2022-05-01) -
Non-stoichiometric compounds : Tungsten bronzes, vanadium bronzes and related compounds /
by: 268227 Bevan, D. J. M., et al.
Published: (1973) -
Hollow Sodium Tungsten Bronze (Na<sub>0.15</sub>WO<sub>3</sub>) Nanospheres: Preparation, Characterization, and Their Adsorption Properties
by: Zuo Guanke, et al.
Published: (2009-01-01) -
Efficient Separation of Silicon and Vanadium by Sodium Roasting-Water Leaching from Vanadium Slag and CaV<sub>2</sub>O<sub>6</sub> Preparation
by: Changqing Li, et al.
Published: (2021-03-01) -
Phase Formation in NaH<sub>2</sub>PO<sub>4</sub>–VOSO<sub>4</sub>–NaF–H<sub>2</sub>O System and Rapid Synthesis of Na<sub>3</sub>V<sub>2</sub>O<sub>2x</sub>(PO<sub>4</sub>)<sub>2</sub>F<sub>3-2x</sub>
by: Zhi Lin
Published: (2023-12-01)