| Summary: | There is limited data assessing the cytotoxic effects of organosolv lignin with cells commonly used in tissue engineering. Structural and physico-chemical characterization of fractionated organosolv lignin showed that a decrease of the molecular weight (MW) is accompanied by a less branched conformation of the phenolic biopolymer (higher S/G ratio) and an increased number of aliphatic hydroxyl functionalities. Enabling stronger polymer−solvent interactions, as proven by the Hansen solubility parameter analysis, low MW organosolv lignin (2543 g/mol) is considered to be compatible with common biomaterials. Using low MW lignin, high cell viability (70–100%) was achieved after 2 h, 24 h and 7 days using the following lignin concentrations: MSCs and osteoblasts (0.02 mg/mL), gingival fibroblasts and keratinocytes (0.02 to 0.04 mg/mL), periodontal ligament fibroblasts and chondrocytes (0.02 to 0.08 mg/mL). Cell viability was reduced at higher concentrations, indicating that high concentrations are cytotoxic. Higher cell viability was attained using 30/70 (<i>w</i>/<i>v</i>) NaOH vs. 40/60 (<i>w</i>/<i>v</i>) EtOH as the initial lignin solvent. Hydrogels containing low MW lignin (0.02 to 0.3 mg/mL) in agarose dose-dependently increased chondrocyte attachment (cell viability 84–100%) and hydrogel viscosity and stiffness to 3–11 kPa, similar to the pericellular matrix of chondrocytes. This suggests that low MW organosolv lignin may be used in many tissue engineering fields.
|
|---|