| Summary: | To enhance the hydrothermal carbonization (HTC) process on biomass waste and improve the quality of biomass solid fuel. Corn straw was pretreated with acid washing and subsequently hydrothermally carbonized at 180–270 °C. The solid product obtained (hydrochars) was compared with the solid product produced from untreated hydrothermally carbonized straw. The results show that the acid pretreatment removed 7.9% of the ash from the straw. ICP and XRD analysis show that most of the alkali and alkaline earth metals have been removed. This addresses the defect of high ash content as the HTC temperature increases. The HHV of hydrochars produced by HTC after acid washing can reach 27.7 MJ/kg, which is nearly 10% higher than that of hydrochars prepared without acid washing pretreatment, and nearly 70% higher than that of straw raw materials. Elemental analysis and FTIR analysis show that the acid washing pretreatment changed the content and structure of the biomass components in the straw, resulting in a more complete HTC reaction and higher carbon sequestration. The decrease of H/C and O/C deepened the degree of coal-like transformation of hydrochars, with the lowest approaching the bituminous coal zone. The combustion characteristics of the hydrochars prepared after acid washing were significantly upgraded, the comprehensive combustion index and thermal stability of hydrochars both increased. Therefore, HTC after acid washing pretreatment is beneficial to further improve the high heating value and combustion characteristics of hydrochar.
|
|---|