Precipitation behavior of a new Cu-Ni-Co-Si-Fe-Mg alloy designed with low cobalt content
A new Cu-1.5Ni-0.7Co-0.7Si-0.3Fe-0.1Mg alloy with low cobalt content was designed. Multi-stage thermo-mechanical treatment (MTT) was used to produce the high-performance alloy with hardness of 286 HV, yield strength of 858 MPa, tensile strength of 910 MPa and electrical conductivity of 45.4 % IACS....