Changes in Abrasive Wear Resistance during Miller Test of High-Manganese Cast Steel with Niobium Carbides Formed in the Alloy Matrix
High-manganese Hadfield cast steel is commonly used for machine components operating under dynamic load conditions. The high fracture toughness and abrasive wear resistance of this steel are the result of an austenitic structure, which—while being ductile—at the same time tends to surface harden und...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2021-05-01
|
| Series: | Applied Sciences |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2076-3417/11/11/4794 |
| _version_ | 1797532945859215360 |
|---|---|
| author | Grzegorz Tęcza |
| author_facet | Grzegorz Tęcza |
| author_sort | Grzegorz Tęcza |
| collection | DOAJ |
| description | High-manganese Hadfield cast steel is commonly used for machine components operating under dynamic load conditions. The high fracture toughness and abrasive wear resistance of this steel are the result of an austenitic structure, which—while being ductile—at the same time tends to surface harden under the effect of cold work. Absence of dynamic loads (e.g., in the case of sand abrasion) causes rapid and premature wear of parts. To improve the abrasive wear resistance of high-manganese cast steel for operation under the conditions free from dynamic loads, primary niobium carbides are produced in this cast steel during the melting process to obtain in castings, after melt solidification, the microstructure consisting of an austenitic matrix and primary niobium carbides uniformly distributed in this matrix. The measured hardness of the tested samples as cast and after solution heat treatment is 260–290 HV and is about 30–60 HV higher than the hardness of common Hadfield cast steel, which is 230 HV. Compared to common Hadfield cast steel, the abrasive wear resistance of the tested high-manganese cast steel measured in the Miller test is at least three times higher at the niobium content of 3.5 wt%. Increasing the niobium content to 4.5 wt%. in the tested samples increases this wear resistance even more. |
| first_indexed | 2024-03-10T11:07:34Z |
| format | Article |
| id | doaj.art-a3a0d5f0953c402bb868fa8c15ba8557 |
| institution | Directory Open Access Journal |
| issn | 2076-3417 |
| language | English |
| last_indexed | 2024-03-10T11:07:34Z |
| publishDate | 2021-05-01 |
| publisher | MDPI AG |
| record_format | Article |
| series | Applied Sciences |
| spelling | doaj.art-a3a0d5f0953c402bb868fa8c15ba85572023-11-21T21:03:29ZengMDPI AGApplied Sciences2076-34172021-05-011111479410.3390/app11114794Changes in Abrasive Wear Resistance during Miller Test of High-Manganese Cast Steel with Niobium Carbides Formed in the Alloy MatrixGrzegorz Tęcza0Department of Cast Alloys and Composites Engineering, Faculty of Foundry Engineering, AGH University of Science and Technology, 23 Reymonta Str., 30-059 Kraków, PolandHigh-manganese Hadfield cast steel is commonly used for machine components operating under dynamic load conditions. The high fracture toughness and abrasive wear resistance of this steel are the result of an austenitic structure, which—while being ductile—at the same time tends to surface harden under the effect of cold work. Absence of dynamic loads (e.g., in the case of sand abrasion) causes rapid and premature wear of parts. To improve the abrasive wear resistance of high-manganese cast steel for operation under the conditions free from dynamic loads, primary niobium carbides are produced in this cast steel during the melting process to obtain in castings, after melt solidification, the microstructure consisting of an austenitic matrix and primary niobium carbides uniformly distributed in this matrix. The measured hardness of the tested samples as cast and after solution heat treatment is 260–290 HV and is about 30–60 HV higher than the hardness of common Hadfield cast steel, which is 230 HV. Compared to common Hadfield cast steel, the abrasive wear resistance of the tested high-manganese cast steel measured in the Miller test is at least three times higher at the niobium content of 3.5 wt%. Increasing the niobium content to 4.5 wt%. in the tested samples increases this wear resistance even more.https://www.mdpi.com/2076-3417/11/11/4794high-manganese cast steelmicrostructureprimary carbideshardnessabrasion |
| spellingShingle | Grzegorz Tęcza Changes in Abrasive Wear Resistance during Miller Test of High-Manganese Cast Steel with Niobium Carbides Formed in the Alloy Matrix Applied Sciences high-manganese cast steel microstructure primary carbides hardness abrasion |
| title | Changes in Abrasive Wear Resistance during Miller Test of High-Manganese Cast Steel with Niobium Carbides Formed in the Alloy Matrix |
| title_full | Changes in Abrasive Wear Resistance during Miller Test of High-Manganese Cast Steel with Niobium Carbides Formed in the Alloy Matrix |
| title_fullStr | Changes in Abrasive Wear Resistance during Miller Test of High-Manganese Cast Steel with Niobium Carbides Formed in the Alloy Matrix |
| title_full_unstemmed | Changes in Abrasive Wear Resistance during Miller Test of High-Manganese Cast Steel with Niobium Carbides Formed in the Alloy Matrix |
| title_short | Changes in Abrasive Wear Resistance during Miller Test of High-Manganese Cast Steel with Niobium Carbides Formed in the Alloy Matrix |
| title_sort | changes in abrasive wear resistance during miller test of high manganese cast steel with niobium carbides formed in the alloy matrix |
| topic | high-manganese cast steel microstructure primary carbides hardness abrasion |
| url | https://www.mdpi.com/2076-3417/11/11/4794 |
| work_keys_str_mv | AT grzegorztecza changesinabrasivewearresistanceduringmillertestofhighmanganesecaststeelwithniobiumcarbidesformedinthealloymatrix |