Feasibility Study on Deposition of Tribaloy T800 on Cobalt-Based L605 Using Micro-Laser-Aided Additive Manufacturing
In this study, deposition of Tribaloy T800 on cobalt-based L605 substrate using micro-laser-aided additive manufacturing (micro-LAAM) was explored. The micro-LAAM process was studied to achieve sound integrity of the deposited layer. The microhardness and microstructure of the deposited Tribaloy T80...
Main Authors: | , , |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2022-03-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/12/4/586 |
_version_ | 1827599917343834112 |
---|---|
author | Lichao Cao Li Zhang Guijun Bi |
author_facet | Lichao Cao Li Zhang Guijun Bi |
author_sort | Lichao Cao |
collection | DOAJ |
description | In this study, deposition of Tribaloy T800 on cobalt-based L605 substrate using micro-laser-aided additive manufacturing (micro-LAAM) was explored. The micro-LAAM process was studied to achieve sound integrity of the deposited layer. The microhardness and microstructure of the deposited Tribaloy T800 layer were investigated. The results showed that the developed micro-LAAM process can achieve single-layer crack-free deposition of Tribaloy T800 onto cobalt-based L605 without pre-heating of the substrate. Surface roughness of Ra 8 μm was obtained, indicating that micro-LAAM can significantly improve the surface quality. Very high microhardness in the range of 818 to 1000 Hv was achieved. Cellular grains with very fine dendritic microstructure and Laves phase were observed in the deposited Tribaloy T800, which contributed to the high hardness. With all the results obtained, it can be concluded that it is feasible to deposit Tribaloy T800 on L605 substrate with micro-LAAM to achieve sound integrity and high hardness. |
first_indexed | 2024-03-09T04:25:06Z |
format | Article |
id | doaj.art-a7dfe5a047c24094ace54fbf544e79fe |
institution | Directory Open Access Journal |
issn | 2075-4701 |
language | English |
last_indexed | 2024-03-09T04:25:06Z |
publishDate | 2022-03-01 |
publisher | MDPI AG |
record_format | Article |
series | Metals |
spelling | doaj.art-a7dfe5a047c24094ace54fbf544e79fe2023-12-03T13:42:16ZengMDPI AGMetals2075-47012022-03-0112458610.3390/met12040586Feasibility Study on Deposition of Tribaloy T800 on Cobalt-Based L605 Using Micro-Laser-Aided Additive ManufacturingLichao Cao0Li Zhang1Guijun Bi2Institute of Intelligent Manufacturing, Guangdong Academy of Sciences, Guangzhou 510070, ChinaInstitute of Intelligent Manufacturing, Guangdong Academy of Sciences, Guangzhou 510070, ChinaInstitute of Intelligent Manufacturing, Guangdong Academy of Sciences, Guangzhou 510070, ChinaIn this study, deposition of Tribaloy T800 on cobalt-based L605 substrate using micro-laser-aided additive manufacturing (micro-LAAM) was explored. The micro-LAAM process was studied to achieve sound integrity of the deposited layer. The microhardness and microstructure of the deposited Tribaloy T800 layer were investigated. The results showed that the developed micro-LAAM process can achieve single-layer crack-free deposition of Tribaloy T800 onto cobalt-based L605 without pre-heating of the substrate. Surface roughness of Ra 8 μm was obtained, indicating that micro-LAAM can significantly improve the surface quality. Very high microhardness in the range of 818 to 1000 Hv was achieved. Cellular grains with very fine dendritic microstructure and Laves phase were observed in the deposited Tribaloy T800, which contributed to the high hardness. With all the results obtained, it can be concluded that it is feasible to deposit Tribaloy T800 on L605 substrate with micro-LAAM to achieve sound integrity and high hardness.https://www.mdpi.com/2075-4701/12/4/586cobalt-based L605 alloyTribaloy T800depositionmicro-laser-aided additive manufacturing |
spellingShingle | Lichao Cao Li Zhang Guijun Bi Feasibility Study on Deposition of Tribaloy T800 on Cobalt-Based L605 Using Micro-Laser-Aided Additive Manufacturing Metals cobalt-based L605 alloy Tribaloy T800 deposition micro-laser-aided additive manufacturing |
title | Feasibility Study on Deposition of Tribaloy T800 on Cobalt-Based L605 Using Micro-Laser-Aided Additive Manufacturing |
title_full | Feasibility Study on Deposition of Tribaloy T800 on Cobalt-Based L605 Using Micro-Laser-Aided Additive Manufacturing |
title_fullStr | Feasibility Study on Deposition of Tribaloy T800 on Cobalt-Based L605 Using Micro-Laser-Aided Additive Manufacturing |
title_full_unstemmed | Feasibility Study on Deposition of Tribaloy T800 on Cobalt-Based L605 Using Micro-Laser-Aided Additive Manufacturing |
title_short | Feasibility Study on Deposition of Tribaloy T800 on Cobalt-Based L605 Using Micro-Laser-Aided Additive Manufacturing |
title_sort | feasibility study on deposition of tribaloy t800 on cobalt based l605 using micro laser aided additive manufacturing |
topic | cobalt-based L605 alloy Tribaloy T800 deposition micro-laser-aided additive manufacturing |
url | https://www.mdpi.com/2075-4701/12/4/586 |
work_keys_str_mv | AT lichaocao feasibilitystudyondepositionoftribaloyt800oncobaltbasedl605usingmicrolaseraidedadditivemanufacturing AT lizhang feasibilitystudyondepositionoftribaloyt800oncobaltbasedl605usingmicrolaseraidedadditivemanufacturing AT guijunbi feasibilitystudyondepositionoftribaloyt800oncobaltbasedl605usingmicrolaseraidedadditivemanufacturing |