Preparation and characterization of low expansion transparent copolyimide films
Five transparent polyimide thin films with different proportions of 1,2,4,5-,pyromellitic dianhydride (PMDA) were made by copolymerization of 4,4'-(six fluoro isopropenyl) two phthalic anhydride (6FDA), 4,4'-two amino -2,2'-double three trifluoromethyl biphenyl (TFMB) and PMDA, and th...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Journal of Materials Engineering
2019-05-01
|
| Series: | Cailiao gongcheng |
| Subjects: | |
| Online Access: | http://jme.biam.ac.cn/CN/Y2019/V47/I5/153 |
| Summary: | Five transparent polyimide thin films with different proportions of 1,2,4,5-,pyromellitic dianhydride (PMDA) were made by copolymerization of 4,4'-(six fluoro isopropenyl) two phthalic anhydride (6FDA), 4,4'-two amino -2,2'-double three trifluoromethyl biphenyl (TFMB) and PMDA, and their properties were characterized. The results show that thermal stability and heat resistance are increased after the introduction of rigid monomers; the dielectric constant of the films is increased with the increase of PMDA content; homopolymer film has higher light transmission rate than copolymer films in visible light; tensile test shows that adding a small amount of PMDA, the tensile strength and elastic modulus of the film are increased, but when the content of PMDA is higher than 40%, the mechanical properties are decreased; the coefficient of thermal expansion of the films are decreased obviously while PMDA content is increased. |
|---|---|
| ISSN: | 1001-4381 1001-4381 |