Case of Crack Dynamics and Wallner Line in Fracture Analysis
Abstract In the case of failure analysis of fracture of crankshaft with material 42CrMo, forged, tempered and nitriding treatment, it is found that there is an abnormal phenomenon of intersection of the scallop lines on the fracture surface. This is not possible in the general fracture surface. The...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Editorial Office of Journal of Mechanical Transmission
2020-05-01
|
| Series: | Jixie chuandong |
| Subjects: | |
| Online Access: | http://www.jxcd.net.cn/thesisDetails#10.16578/j.issn.1004.2539.2020.05.029 |
| _version_ | 1826881433598164992 |
|---|---|
| author | Xiaolu Zhu |
| author_facet | Xiaolu Zhu |
| author_sort | Xiaolu Zhu |
| collection | DOAJ |
| description | Abstract In the case of failure analysis of fracture of crankshaft with material 42CrMo, forged, tempered and nitriding treatment, it is found that there is an abnormal phenomenon of intersection of the scallop lines on the fracture surface. This is not possible in the general fracture surface. The crack dynamics and the theory of Wallner line are used to analyze the abnormal phenomenon, the crack at the source of fracture fatigue will produce stress wave in the material and propagate on the surface where the crack is located. When the crack encounters a discontinuous surface, a transverse stress wave is generated, thus forming a second set of concentric arcs centered at the wave source. This makes it possible for the shellfish lines to intersect. For the first time, it is observed that Wallner line cannot only appear on fracture surfaces of metallic and non-metallic brittle materials. It illustrates that Wallner line can also appear on the fracture surface of quenched and tempered steel. |
| first_indexed | 2024-03-13T09:25:25Z |
| format | Article |
| id | doaj.art-a8cfac78a82a48768709aefaf0dbdca6 |
| institution | Directory Open Access Journal |
| issn | 1004-2539 |
| language | zho |
| last_indexed | 2025-02-17T02:45:00Z |
| publishDate | 2020-05-01 |
| publisher | Editorial Office of Journal of Mechanical Transmission |
| record_format | Article |
| series | Jixie chuandong |
| spelling | doaj.art-a8cfac78a82a48768709aefaf0dbdca62025-01-10T14:55:48ZzhoEditorial Office of Journal of Mechanical TransmissionJixie chuandong1004-25392020-05-014417618029796496Case of Crack Dynamics and Wallner Line in Fracture AnalysisXiaolu ZhuAbstract In the case of failure analysis of fracture of crankshaft with material 42CrMo, forged, tempered and nitriding treatment, it is found that there is an abnormal phenomenon of intersection of the scallop lines on the fracture surface. This is not possible in the general fracture surface. The crack dynamics and the theory of Wallner line are used to analyze the abnormal phenomenon, the crack at the source of fracture fatigue will produce stress wave in the material and propagate on the surface where the crack is located. When the crack encounters a discontinuous surface, a transverse stress wave is generated, thus forming a second set of concentric arcs centered at the wave source. This makes it possible for the shellfish lines to intersect. For the first time, it is observed that Wallner line cannot only appear on fracture surfaces of metallic and non-metallic brittle materials. It illustrates that Wallner line can also appear on the fracture surface of quenched and tempered steel.http://www.jxcd.net.cn/thesisDetails#10.16578/j.issn.1004.2539.2020.05.029Fracture analysis |
| spellingShingle | Xiaolu Zhu Case of Crack Dynamics and Wallner Line in Fracture Analysis Jixie chuandong Fracture analysis |
| title | Case of Crack Dynamics and Wallner Line in Fracture Analysis |
| title_full | Case of Crack Dynamics and Wallner Line in Fracture Analysis |
| title_fullStr | Case of Crack Dynamics and Wallner Line in Fracture Analysis |
| title_full_unstemmed | Case of Crack Dynamics and Wallner Line in Fracture Analysis |
| title_short | Case of Crack Dynamics and Wallner Line in Fracture Analysis |
| title_sort | case of crack dynamics and wallner line in fracture analysis |
| topic | Fracture analysis |
| url | http://www.jxcd.net.cn/thesisDetails#10.16578/j.issn.1004.2539.2020.05.029 |
| work_keys_str_mv | AT xiaoluzhu caseofcrackdynamicsandwallnerlineinfractureanalysis |